Microstructure and mechanical properties of laminated Nb/Ti3Al(Si)C2-TiC-Al2O3 composites
| Parent link: | Journal of Materials Science.— .— New York: Springer Science+Business Media LLC. Vol. 60, iss. 45.— 2025.— P. 22688-22700 |
|---|---|
| مؤلفون آخرون: | , , , , |
| الملخص: | Title screen In this work, laminated Nb/Ti3Al(Si)C2-TiC-Al2O3 metal-ceramic composites were fabricated for the first time using the hot-pressing (HP) method. The starting materials consisted of Nb metal foils and Ti3Al(Si)C2 highly filled preceramic papers. The composites were sintered at 1250 °C under 50 MPa for 60 min. The microstructure and phase composition were studied using scanning electron microscopy and X-ray diffraction, while the mechanical properties were evaluated through Vickers method and three-point bending tests. The obtained results were compared with those of composites fabricated by spark plasma sintering (SPS). A heterophase reaction layer with an average thickness of 22 μm was formed at the ceramic/metal interface, which was slightly thicker than that obtained by SPS. The stronger decomposition of the MAX phase during HP inhibited densification and altered interfacial reaction kinetics. The obtained quasi-ductility (deformation up to 5%) can be explained by the delocalized plastic deformation of Nb layers caused by multiple cracks in Ti3Al(Si)C2-based layers Текстовый файл AM_Agreement |
| اللغة: | الإنجليزية |
| منشور في: |
2025
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | https://doi.org/10.1007/s10853-025-11731-7 |
| التنسيق: | الكتروني فصل الكتاب |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=684700 |