Barrier Properties of Cr/Ta-Coated Zr-1Nb Alloy under High-Temperature Oxidation
| Parent link: | Metals.— .— Basel: MDPI AG Vol. 14, iss. 6.— 2024.— Article number 645, 17 p. |
|---|---|
| Corporate Author: | |
| Other Authors: | , , , , , |
| Summary: | In this paper, Cr (8 μm)/Ta (3 μm) bilayer coatings deposited on a Zr-1Nb alloy substrate were investigated and compared with a Cr-coated alloy under high-temperature steam oxidation at 1200–1400 °C. The bilayer coatings with α- and β-Ta interlayers were obtained by magnetron sputtering. The Cr/Ta-coated samples were studied using scanning electron microscopy (SEM), X-ray diffraction (XRD), and optical microscopy (OM). The coating with an α-Ta interlayer can suppress the interdiffusion of chromium and zirconium more effectively up to 1330 °C in comparison with the coating having a β-Ta interlayer. The weight gain of the α-Ta-coated samples after oxidation at 1200 °C for 2000 s was 5–6 times lower than that of the Cr-coated Zr alloy samples. Oxidation at 1400 °C for 120 s showed no significant difference in the weight gain of the Cr- and Cr/Ta-coated Zr-1Nb alloy samples. It was shown that the effect of suppression of Zr-Cr interdiffusion by the barrier coating (α- and β-Ta) is only short-term. Текстовый файл |
| Language: | English |
| Published: |
2024
|
| Subjects: | |
| Online Access: | https://doi.org/10.3390/met14060645 |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=674346 |