Стойкость циркониевого сплава Zr–1Nb С Cr/Mo покрытием при высокотемпературном окислении в потоке водяного пара
| Parent link: | Курзина, И. А. (химик ; 1972-). Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XX Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 25-28 апреля 2023 г..— .— Томск: Изд-во ТПУ, 2023 Т. 1 : Физика.— 2023.— С. 15-17 |
|---|---|
| Main Author: | |
| Corporate Author: | |
| Other Authors: | |
| Summary: | Заглавие с экрана The resistance of Cr/Mo-coated Zr–1Nb zirconium alloy under high-temperature steam oxidation was investigated. The bilayer Cr (8 μm)/Mo (3 μm) coatings were produced by magnetron sputtering. High-temperature tests were carried out at 1200, 1330 and 1400 °C at different oxidation durations. The Mo sublayer limits the mutual diffusion of Cr-Zr at 1200 and 1330 °C for at least 2000 and 720 s, respectively. The weight gain of sample at 1400 °C was comparable to the single-layer Cr coating Текстовый файл |
| Published: |
2023
|
| Subjects: | |
| Online Access: | http://earchive.tpu.ru/handle/11683/80784 |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=670021 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 670021 | ||
| 005 | 20241031131421.0 | ||
| 090 | |a 670021 | ||
| 100 | |a 20231214d2023 k||y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 200 | 1 | |a Стойкость циркониевого сплава Zr–1Nb С Cr/Mo покрытием при высокотемпературном окислении в потоке водяного пара |f А. В. Абдульменова |g науч. рук. Е. Б. Кашкаров ; Инженерная школа ядерных технологий НИ ТПУ |d Resistance of Cr/Mo-coated Zr–1Nb alloy under high-temperature steam oxidation |z eng | |
| 300 | |a Заглавие с экрана | ||
| 320 | |a Библиография: с. 17 | ||
| 330 | |a The resistance of Cr/Mo-coated Zr–1Nb zirconium alloy under high-temperature steam oxidation was investigated. The bilayer Cr (8 μm)/Mo (3 μm) coatings were produced by magnetron sputtering. High-temperature tests were carried out at 1200, 1330 and 1400 °C at different oxidation durations. The Mo sublayer limits the mutual diffusion of Cr-Zr at 1200 and 1330 °C for at least 2000 and 720 s, respectively. The weight gain of sample at 1400 °C was comparable to the single-layer Cr coating | ||
| 336 | |a Текстовый файл | ||
| 461 | 1 | |0 636133 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XX Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 25-28 апреля 2023 г. |d 2023 |9 636133 |a Курзина, И. А. (химик ; 1972-) |c Томск |n Изд-во ТПУ | |
| 463 | 1 | |0 669915 |t Т. 1 : Физика |v С. 15-17 |d 2023 |9 669915 |p 1 файл (75,9 MB, 442 с.) |u conference_tpu-2023-C21_V1.pdf |l Volume 1. Physics | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a циркониевые сплавы | |
| 610 | 1 | |a высокотемпературное окисление | |
| 610 | 1 | |a покрытия | |
| 700 | 1 | |a Абдульменова |b А. В. |c физик |c инженер Томского политехнического университета |f 2001- |g Анастасия Владимировна |9 88515 | |
| 702 | 1 | |a Кашкаров |b Е. Б. |c физик |c доцент, научный сотрудник Томского политехнического университета, кандидат физико-математических наук |f 1991- |g Егор Борисович |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа ядерных технологий |b Отделение экспериментальной физики |9 28346 |
| 801 | 0 | |a RU |b 63413507 |c 20231213 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/80784 |z http://earchive.tpu.ru/handle/11683/80784 | |
| 942 | |c CF | ||