Стойкость циркониевого сплава Zr–1Nb С Cr/Mo покрытием при высокотемпературном окислении в потоке водяного пара
| Parent link: | Курзина, И. А. (химик ; 1972-). Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XX Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 25-28 апреля 2023 г..— .— Томск: Изд-во ТПУ, 2023 Т. 1 : Физика.— 2023.— С. 15-17 |
|---|---|
| Main Author: | |
| Corporate Author: | |
| Other Authors: | |
| Summary: | Заглавие с экрана The resistance of Cr/Mo-coated Zr–1Nb zirconium alloy under high-temperature steam oxidation was investigated. The bilayer Cr (8 μm)/Mo (3 μm) coatings were produced by magnetron sputtering. High-temperature tests were carried out at 1200, 1330 and 1400 °C at different oxidation durations. The Mo sublayer limits the mutual diffusion of Cr-Zr at 1200 and 1330 °C for at least 2000 and 720 s, respectively. The weight gain of sample at 1400 °C was comparable to the single-layer Cr coating Текстовый файл |
| Published: |
2023
|
| Subjects: | |
| Online Access: | http://earchive.tpu.ru/handle/11683/80784 |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=670021 |