The Microstructural and Phase Evolution of the 3D Printed Ti-6Al-4V Alloy during Mechanical Loading
Saved in:
| Parent link: | Physics of Metals and Metallography Vol. 124, iss. 2.— 2023.— [P. 217-223] |
|---|---|
| Andre forfattere: | , , , , |
| Summary: | Title screen This paper presents the results of an in situ study on the evolution of the microstructure and phase composition of 3D-printed Ti-6Al-4V samples under tension in the transmission electron microscope column. The microstructure of Ti-6Al-4V specimens manufactured by wire-feed electron beam additive technology is shown to consist of columnar primary β-grains inside of which are α/α'-Ti laths separated by layers of the residual β-phase and gathered into packets. A characteristic feature of 3D-printed Ti-6Al-4V samples is the concentration nonuniformity of the alloying elements due to the partial decomposition of the martensitic α'-phase. The reorientation of the α/α'-Ti lattice near interfaces takes place during uniaxial tension. Deformation-induced α'→α" transformations can develop in the reoriented regions of the α/α'-Ti lattice, in places enriched in vanadium. Режим доступа: по договору с организацией-держателем ресурса |
| Sprog: | engelsk |
| Udgivet: |
2023
|
| Fag: | |
| Online adgang: | https://doi.org/10.1134/S0031918X23700114 |
| Format: | Electronisk Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=669586 |
| Tags: |
Tilføj Tag
Ingen Tags, Vær først til at tagge denne postø!
|