Investigation of the influence of the mode of heat treatment of the initialpowder on the efficiency of sintering zirconium ceramics by dilatometry; Вестник Карагандинского университета. Серия Физика; № 3 (103)
| Parent link: | Вестник Карагандинского университета. Серия Физика № 3 (103).— 2021.— [С. 17-24] |
|---|---|
| Hlavní autor: | |
| Korporativní autor: | |
| Další autoři: | , |
| Shrnutí: | Using methods of synchronous thermal and X-ray structural analyzes applied to zirconium dioxide powders partially stabilized with yttrium obtained by chemical coprecipitation the processes of dehydration of these powders during annealing in air have been investigated. Using the dilatometry method, the regularities ofcompaction of powder compacts have been investigated with thermal sintering. It was found that the resulting powders mainly consist of the tetragonal modification zirconium dioxide and are nano-sized. The average particle size was 25 nm. The resulting powders are characterized by a high degree of agglomeration. It isshown that an increase in the thermal annealing temperature from 500 to 700є? leads to partial baking of individual particles inside the agglomerate, and causes the formation of hard agglomerates, the presence of which complicates the processes of compaction and subsequent sintering. The presence of such agglomerates prevents the production of ceramics with high mechanical characteristics: density and porosity. Thermal annealing temperature increase leads to a decrease in the density of the sintered ceramic and a decrease in its hardness. С использованием методов синхронного термического и рентгеноструктурного анализа применительно к порошкам диоксида циркония, частично стабилизированного иттрием, полученных методом химического соосаждения, исследованы процессы дегидратации этих порошков при отжиге на воздухе. При помощи метода дилатометрии изучены закономерности уплотнения порошковых компактов при термическом спекании. Установлено, что полученные порошки состоят преимущественно из тетрагональной модификации диоксида циркония и имеют наноразмеры. Средний размер частиц - 25 нм. При этом полученные порошки характеризуются высокой степенью агломерации. Показано, что увеличение температуры термического отжига с 500 до 700 ºС приводит к частичному припеканию отдельных частиц внутри агломерата, и вызывает формирование жестких агломератов, наличие которых затрудняет процессы компактирования и последующего спекания. Наличие подобных агломератов препятствует получению керамики с высокими механическими характеристиками: плотностью и пористостью. Повышение температуры термического отжига приводит к снижению плотности спеченной керамики и снижению ее твердости. |
| Jazyk: | angličtina |
| Vydáno: |
2021
|
| Témata: | |
| On-line přístup: | https://doi.org/10.31489/2021Ph3/17-24 |
| Médium: | Elektronický zdroj Kapitola |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=667186 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 667186 | ||
| 005 | 20250304140542.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\38391 | ||
| 035 | |a RU\TPU\network\38168 | ||
| 090 | |a 667186 | ||
| 100 | |a 20220302d2021 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a KZ | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Investigation of the influence of the mode of heat treatment of the initialpowder on the efficiency of sintering zirconium ceramics by dilatometry |d Исследование влияния режима термической обработки исходного порошка на эффективность спекания циркониевой керамики методом дилатометрии |f S. A. Shevelev, E. A. Sheveleva, O. Stary | |
| 203 | |a Text |c electronic | ||
| 320 | |a [Библиогр.: 31 назв.] | ||
| 330 | |a Using methods of synchronous thermal and X-ray structural analyzes applied to zirconium dioxide powders partially stabilized with yttrium obtained by chemical coprecipitation the processes of dehydration of these powders during annealing in air have been investigated. Using the dilatometry method, the regularities ofcompaction of powder compacts have been investigated with thermal sintering. It was found that the resulting powders mainly consist of the tetragonal modification zirconium dioxide and are nano-sized. The average particle size was 25 nm. The resulting powders are characterized by a high degree of agglomeration. It isshown that an increase in the thermal annealing temperature from 500 to 700є? leads to partial baking of individual particles inside the agglomerate, and causes the formation of hard agglomerates, the presence of which complicates the processes of compaction and subsequent sintering. The presence of such agglomerates prevents the production of ceramics with high mechanical characteristics: density and porosity. Thermal annealing temperature increase leads to a decrease in the density of the sintered ceramic and a decrease in its hardness. | ||
| 330 | |a С использованием методов синхронного термического и рентгеноструктурного анализа применительно к порошкам диоксида циркония, частично стабилизированного иттрием, полученных методом химического соосаждения, исследованы процессы дегидратации этих порошков при отжиге на воздухе. При помощи метода дилатометрии изучены закономерности уплотнения порошковых компактов при термическом спекании. Установлено, что полученные порошки состоят преимущественно из тетрагональной модификации диоксида циркония и имеют наноразмеры. Средний размер частиц - 25 нм. При этом полученные порошки характеризуются высокой степенью агломерации. Показано, что увеличение температуры термического отжига с 500 до 700 ºС приводит к частичному припеканию отдельных частиц внутри агломерата, и вызывает формирование жестких агломератов, наличие которых затрудняет процессы компактирования и последующего спекания. Наличие подобных агломератов препятствует получению керамики с высокими механическими характеристиками: плотностью и пористостью. Повышение температуры термического отжига приводит к снижению плотности спеченной керамики и снижению ее твердости. | ||
| 461 | |t Вестник Карагандинского университета. Серия Физика | ||
| 463 | |t № 3 (103) |v [С. 17-24] |d 2021 | ||
| 510 | 1 | |a Исследование влияния режима термической обработки исходного порошка на эффективность спекания циркониевой керамики методом дилатометрии |z rus | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a zirconium dioxide | |
| 610 | 1 | |a dilatometry | |
| 610 | 1 | |a co-precipitation | |
| 610 | 1 | |a chlorides | |
| 610 | 1 | |a microscopy | |
| 610 | 1 | |a agglomeration | |
| 610 | 1 | |a диоксид циркония | |
| 610 | 1 | |a дилатометрия | |
| 610 | 1 | |a соосаждение | |
| 610 | 1 | |a хлориды | |
| 610 | 1 | |a микроскопия | |
| 610 | 1 | |a агломерация | |
| 700 | 1 | |a Shevelev |b S. A. |c specialist in the field of heat and power engineering |c senior lecturer of Tomsk Polytechnic University |f 1983- |g Sergey Anatolievich |3 (RuTPU)RU\TPU\pers\36037 |9 19174 | |
| 701 | 1 | |a Sheveleva |b E. A. |c specialist in the field of electrical engineering |c Associate Professor of Tomsk Polytechnic University, Candidate of technical sciences |f 1975- |g Elena Aleksandrovna |3 (RuTPU)RU\TPU\pers\42239 |9 21500 | |
| 701 | 1 | |a Stary |b O. |c Specialist in the field of non-destructive testing |c Senior researcher of Tomsk Polytechnic University, Candidate of economic sciences |f 1960- |g Oldrich |3 (RuTPU)RU\TPU\pers\45340 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа энергетики |b Научно-образовательный центр И. Н. Бутакова (НОЦ И. Н. Бутакова) |3 (RuTPU)RU\TPU\col\23504 |
| 801 | 1 | |a RU |b 63413507 |c 20130530 | |
| 801 | 2 | |a RU |b 63413507 |c 20220302 |g RCR | |
| 856 | 4 | |u https://doi.org/10.31489/2021Ph3/17-24 | |
| 942 | |c CF | ||