Single SOFC with Supporting Ni-YSZ Anode, Bilayer YSZ/GDC Film Electrolyte, and La2NiO4+delta Cathode
| Parent link: | Russian Journal of Electrochemistry Vol. 54, iss. 6.— 2018.— [P. 541–546] |
|---|---|
| מחבר תאגידי: | |
| מחברים אחרים: | , , , , , , , , |
| סיכום: | Title screen Characteristics of fuel cells with supporting Ni-YSZ anode, bilayer YSZ/GDC electrolyte with the thickness of 10 [mu]m, and La2NiO4+[sigma] cathode are studied. It is shown that when humid (3% water) hydrogen is supplied to the anode and air is supplied to the cathode, the maximum values of cell's power density are 1.05 and 0.75 W/cm2 at 900 and 800°С, respectively. After the introduction of praseodymium oxide and ceria into the cathode and the anode, respectively, the power density is ca. 1 W/cm2 at 700°С. It is found that the power density of a cell with impregnated electrodes weakly increases with the increase in temperature to ca. 1.4 W/cm2 at 900°С. The analysis of impedance spectra by the distribution of relaxation times shows that such behavior is associated with the gas-diffusion resistance of the SOFC anode. The latter is explained by the low porosity of the anode and the high rate of fuel consumption. Режим доступа: по договору с организацией-держателем ресурса |
| יצא לאור: |
2018
|
| נושאים: | |
| גישה מקוונת: | https://doi.org/10.1134/S1023193518060101 |
| פורמט: | אלקטרוני Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=665862 |