Combustion Synthesis of Sialon and Nitride Phases Based on Ferrosilicoaluminum with Marshalite Additives

Combustion Synthesis of Sialon and Nitride Phases Based on Ferrosilicoaluminum with Marshalite Additives

التفاصيل البيبلوغرافية
Parent link:Refractories and Industrial Ceramics
Vol. 61, iss. 6.— 2021.— [P. 655-658]
مؤلف مشترك: Национальный исследовательский Томский политехнический университет Инженерная школа новых производственных технологий Научно-образовательный центр Н. М. Кижнера
مؤلفون آخرون: Bolgaru K. A. Konstantin Aleksandrovich, Vereshchagin (Vereschagin, Vereshagin) V. I. Vladimir Ivanovich, Reger A. A. Anton Andreevich, Skvortsova L. N. Lidiya Nikolaevna
الملخص:Title screen
The effect of a marshalite additive on nitriding of a complex ferrosilicoaluminum (FSA) ferroalloy to produce a sialon-based composite by self-propagating high-temperature synthesis is studied. The phase composition of the combustion products is revealed by changing the percentage of the marshalite additive in the starting reaction mixture. The optimal ratio of the marshalite additive to the initial FSApowder to obtain a product with the maximum sialon content is established.
Режим доступа: по договору с организацией-держателем ресурса
منشور في: 2021
الموضوعات:
электронный ресурс
труды учёных ТПУ
marshalite
sialon
ferrosilicoaluminum (FSA)
self-propagating high-temperature synthesis (SHS)
nitriding
filtration combustion
маршалиты
сиалон
ферросиликоалюминий
самораспространяющийся высокотемпературный синтез
азотирование
фильтрационное горение
الوصول للمادة أونلاين:https://doi.org/10.1007/s11148-021-00537-0
التنسيق: الكتروني فصل الكتاب
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=665861

الانترنت

https://doi.org/10.1007/s11148-021-00537-0

مواد مشابهة