MgAl2O4 ceramics doped with rare earth ions: Synthesis and luminescent properties
| Parent link: | AIP Conference Proceedings Vol. 2174 : Physics, Technologies and Innovation (PTI-2019).— 2019.— [020262, 6 p.] |
|---|---|
| Altri autori: | , , , , |
| Riassunto: | Title screen Transparent magnesium aluminate spinel (MgAl2O4) ceramics doped with Ce3+ and Tb3+ ions were fabricated by Spark Plasma Sintering (SPS) technique. Complex characterization of the optical and photoluminescent properties of the sintered ceramic was carried out. The redshift in the in-line transmittance spectrum for RE ions doped spinel ceramics is observed. The photoluminescence spectrum excited by nitrogen laser consists of broad emission band with a maximum at ?em = 435 nm for the MAS:0.1Ce ceramics The possible nature of this luminescence can be due to radiative transitions in the cerium ions from 5d to 4f level. There are a series of emission bands in 400 – 700 nm spectral range for MAS:0.1Tb ceramics. In the “blue” spectral region the complex host centers such as F-type centers are recorded. The luminescence decay kinetics analysis for all ceramics samples is performed. The effect of cerium and terbium oxide on the optical, photoluminescent properties of MgAl2O4-based transparent ceramics is discussed. Режим доступа: по договору с организацией-держателем ресурса |
| Pubblicazione: |
2019
|
| Soggetti: | |
| Accesso online: | https://doi.org/10.1063/1.5134413 |
| Natura: | Elettronico Capitolo di libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=662429 |