Surface modification of selective laser melted Ti-6Al-4V by ultrasonic impact treatment and electron beam irradiation; AIP Conference Proceedings; Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19)
| Parent link: | AIP Conference Proceedings Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19).— 2019.— [020336, 5 p.] |
|---|---|
| Glavni autor: | |
| Autor kompanije: | |
| Daljnji autori: | , |
| Sažetak: | Title screen Changes of the surface roughness, microstructure, phase composition and microhardness of selective laser melted Ti-6Al-4V samples during electron beam irradiation and ultrasonic impact treatment were investigated by contact profilometry, optical microscopy, X-ray analysis, and hardness measurement. It was shown that electron beam irradiation and ultrasonic impact treatment of the selective laser melted Ti-6Al-4V samples smooth their surface. Significant refinement of the microstructure and TiO nanoparticles formation under ultrasonic impact treatment occur causing the increase in surface microhardness. Electron beam irradiation leads to a more significant increase in both the microhardness and thickness of the melted surface layer due to martensitic transformation. Режим доступа: по договору с организацией-держателем ресурса |
| Jezik: | engleski |
| Izdano: |
2019
|
| Teme: | |
| Online pristup: | https://doi.org/10.1063/1.5132203 |
| Format: | Elektronički Poglavlje knjige |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=661549 |
| Sažetak: | Title screen Changes of the surface roughness, microstructure, phase composition and microhardness of selective laser melted Ti-6Al-4V samples during electron beam irradiation and ultrasonic impact treatment were investigated by contact profilometry, optical microscopy, X-ray analysis, and hardness measurement. It was shown that electron beam irradiation and ultrasonic impact treatment of the selective laser melted Ti-6Al-4V samples smooth their surface. Significant refinement of the microstructure and TiO nanoparticles formation under ultrasonic impact treatment occur causing the increase in surface microhardness. Electron beam irradiation leads to a more significant increase in both the microhardness and thickness of the melted surface layer due to martensitic transformation. Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| Digitalni identifikator objekta: | 10.1063/1.5132203 |