Surface modification of selective laser melted Ti-6Al-4V by ultrasonic impact treatment and electron beam irradiation
| Parent link: | AIP Conference Proceedings Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19).— 2019.— [020336, 5 p.] |
|---|---|
| Hoofdauteur: | |
| Coauteur: | |
| Andere auteurs: | , |
| Samenvatting: | Title screen Changes of the surface roughness, microstructure, phase composition and microhardness of selective laser melted Ti-6Al-4V samples during electron beam irradiation and ultrasonic impact treatment were investigated by contact profilometry, optical microscopy, X-ray analysis, and hardness measurement. It was shown that electron beam irradiation and ultrasonic impact treatment of the selective laser melted Ti-6Al-4V samples smooth their surface. Significant refinement of the microstructure and TiO nanoparticles formation under ultrasonic impact treatment occur causing the increase in surface microhardness. Electron beam irradiation leads to a more significant increase in both the microhardness and thickness of the melted surface layer due to martensitic transformation. Режим доступа: по договору с организацией-держателем ресурса |
| Taal: | Engels |
| Gepubliceerd in: |
2019
|
| Onderwerpen: | |
| Online toegang: | https://doi.org/10.1063/1.5132203 |
| Formaat: | Elektronisch Hoofdstuk |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=661549 |