Structural Transformations in Air Heated Al-Cr Powder Compacts; AIP Conference Proceedings; Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19)
| Parent link: | AIP Conference Proceedings Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19).— 2019.— [020289, 5 p.] |
|---|---|
| Autor principal: | |
| Autor corporatiu: | |
| Altres autors: | , |
| Sumari: | Title screen In this study, structural changes in aluminum- chromium powder compacts were considered during exposure in the air at 500 °C. The samples were obtained by pressing the mixture of aluminum and chromium powders. The studies were carried out with using the X-ray diffraction and the metallographic analysis and by measuring the weight gain of the samples. It was established that the value of the specific mass gain has a complex and ambiguous dependence on the initial porosity of Al-Cr compacts due to phase transformations in powder mixtures. At short-term (up to 30 minutes) 500 °C air heating of the porous compacts significant oxidation does not occur. However, at the long-term exposure at 500 °C the reaction diffusion between aluminum and chromium occurs resulting in Al[13]Cr[2] intermetallic formation and compacts swelling. Режим доступа: по договору с организацией-держателем ресурса |
| Idioma: | anglès |
| Publicat: |
2019
|
| Matèries: | |
| Accés en línia: | https://doi.org/10.1063/1.5132156 |
| Format: | Electrònic Capítol de llibre |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=661538 |