Investigation of the Effect of Structural and Phase State of the ZrO[2] Ceramics on Thermal Shock Resistance

Opis bibliograficzny
Parent link:AIP Conference Proceedings
Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19).— 2019.— [020229, 4 p.]
Korporacja: Национальный исследовательский Томский политехнический университет Инженерная школа новых производственных технологий Отделение материаловедения
Kolejni autorzy: Mirovoy Yu. A. Yury Aleksandrovich, Burlachenko A. G., Dedova E. S. Elena Sergeevna, Derkach E. A., Buyakova S. P. Svetlana Petrovna
Streszczenie:Title screen
The influence of thermal shock loading on the phase composition and microstructure of the ZrO[2](Y[2]O[3]) ceramics was studied. It was found that thermal shock strains had no effect on phase composition of ZrO[2](Y[2]O[3]) ceramics. The reducing of concentration of high-temperature tetragonal t-ZrO[2] and the increase in content of lowtemperature monoclinic m-ZrO[2] crystal system with each subsequent thermal shock loading was observed. The formation of block structure in all studied ceramics was observed. The sizes of the blocks formed in the ZrO[2](Y[2]O[3]) ceramics were slightly different. The formation of the blocks in ceramics occurred on the grain boundaries.
Режим доступа: по договору с организацией-держателем ресурса
Język:angielski
Wydane: 2019
Hasła przedmiotowe:
Dostęp online:https://doi.org/10.1063/1.5132096
Format: Elektroniczne Rozdział
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=661518