High-temperature modification of sibunit for its application as a support for ruthenium catalysts in ammonia synthesis; AIP Conference Proceedings; Vol. 2141 : Oil and Gas Engineering (OGE-2019)
| Parent link: | AIP Conference Proceedings Vol. 2141 : Oil and Gas Engineering (OGE-2019).— 2019.— [020017, 6 p.] |
|---|---|
| Autor corporatiu: | |
| Altres autors: | , , , , , , |
| Sumari: | Title screen The effect of high-temperature (1400-2200°C) treatment of the carbon material Sibunit on its structural properties was studied. High-temperature treatment leads to structural ordering of the initial Sibunit. As a result of preliminary graphitization, specific surface area decreases by a factor of 10, but thermal stability increases. A good correlation between XRD, Raman spectroscopy and TGA data is observed. For the Sibunit sample treated at 2200 °C, the interplanar distance d(002) estimated by XRD decreases by 0.05 Е in comparison with the initial Sibunit, ID/IG decreases from 1.59 to 1.18, and the 2D line substantially increases, which testify to the structural ordering. According to TGA, the temperatures corresponding to the onset of oxidation, 50% oxidation and the end of oxidation of Sibunit calcined at 2200 °C are synchronously shifted by 100 °C with respect to the initial Sibunit. Режим доступа: по договору с организацией-держателем ресурса |
| Idioma: | anglès |
| Publicat: |
2019
|
| Matèries: | |
| Accés en línia: | https://doi.org/10.1063/1.5122036 |
| Format: | Electrònic Capítol de llibre |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=660626 |