Hardness and Abrasive Wear Resistance of Electron Beam Coatings Cladded by Using of "TiB-Titanium Matrix" Composite Powders
| Parent link: | AIP Conference Proceedings Vol. 2051 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2018 (AMHS’18).— 2018.— [020137, 5 p.] |
|---|---|
| Kolejni autorzy: | , , , , |
| Streszczenie: | Title screen The paper describes the structure, hardness and wear resistance of electron beam coatings cladded by using of "TiB-titanium binder" composite powders. The powders have been synthesized from titanium and boron powder mixtures by self-propagating high temperature synthesis (SHS) at wave burning mode. The SHS powders were cladded on titanium substrate VT1-0 by electron beam surfacing. A phase composition and a structure of the SHS powders and of the cladded coatings were investigated by X-ray diffraction and optical microscopy. According to structure investigation and hardness measurement in the "coating-titanium base plate" transition zone an adhesion between the coating and the substrate was high. The maximum hardness increase of the coatings strengthened by needle-like titanium monoboride inclusions was 2.2 times and abrasive wear resistance-3.7 times as compared with VT1-0 titanium. Режим доступа: по договору с организацией-держателем ресурса |
| Język: | angielski |
| Wydane: |
2018
|
| Hasła przedmiotowe: | |
| Dostęp online: | https://doi.org/10.1063/1.5083380 |
| Format: | Elektroniczne Rozdział |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=659183 |