Properties of the Zirconia Nanopowders Synthesized by the Chemical Precipitation Method after Long-Time Keeping; AIP Conference Proceedings; Vol. 2051 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2018 (AMHS’18)

Properties of the Zirconia Nanopowders Synthesized by the Chemical Precipitation Method after Long-Time Keeping; AIP Conference Proceedings; Vol. 2051 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2018 (AMHS’18)

Bibliographic Details
Parent link:AIP Conference Proceedings
Vol. 2051 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2018 (AMHS’18).— 2018.— [020124, 4 p.]
Main Author: Klevtsova E. V. Ekaterina
Corporate Author: Национальный исследовательский Томский политехнический университет Инженерная школа новых производственных технологий Отделение материаловедения
Other Authors: Kulkov S. N. Sergey Nikolaevich
Summary:Title screen
The structure and properties of ZrO[2-3] mol. % Y2O3 powders synthesized by the chemical precipitation method using ultrasonic treatment, subjected to the long-time stored under normal conditions for 2´108 s (7 years), are investigated. It is shown that the morphology of the powder particles after long-time keeping in normal conditions has changed relative to the initial one. The particle size of the powder after keeping in the case of conventional synthesis is increased by 1.5 times, in the case of using ultrasonic treatment during the synthesis-decreases by 18 times. It is found that the change in the specific surface area after keeping process occurs only in the powder synthesized with ultrasonic treatment in the initial powders without annealing. Subsequent anneals completely restore the state of the aged powder to its original state. The phase composition of the powders in the initial state is represented by the tetragonal modification of ZrO[2], whereas the phase composition of the keeped ZrO[2]-Y[2]O[3] powders has the tetragonal and cubic phases, and amount of cubic phase is approximately 5-20%, depending on the annealing temperature. Thus, a change in the morphology and particle size of the powder after keeping leads to additional stabilization of zirconium.
Режим доступа: по договору с организацией-держателем ресурса
Language:English
Published: 2018
Subjects:
электронный ресурс
труды учёных ТПУ
нанопорошки
диоксид циркония
химическое осаждение
ультразвуковая обработка
отжиг
фазовый состав
синтез
Online Access:https://doi.org/10.1063/1.5083367
Format: Electronic Book Chapter
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=659178