One-step synthesis of nitrogen-doped carbon nanofibers from melamine over nickel alloy in a closed system

Xehetasun bibliografikoak
Parent link:Chemical Physics Letters
Vol. 685.— 2017.— [P. 259-262]
Egile korporatiboa: Национальный исследовательский Томский политехнический университет Инженерная школа энергетики Научно-образовательный центр И. Н. Бутакова (НОЦ И. Н. Бутакова), Национальный исследовательский Томский политехнический университет Исследовательская школа химических и биомедицинских технологий (ИШХБМТ)
Beste egile batzuk: Kenzhin R. M., Bauman Y. Yury, Volodin A. M. Aleksandr M., Mishakov I. V. Iljya Vladimirovich, Vedyagin A. A. Aleksey Anatolievich
Gaia:Title screen
A novel approach to the synthesis of nitrogen-doped carbon nanofibers in a closed system at elevated pressure with the use of bulk Ni-Cr alloy as a catalyst precursor was proposed. Melamine was chosen as a substrate containing both carbon and nitrogen. Method of ferromagnetic resonance was applied for diagnostics of dispersed Ni particles appearance. The process of corrosion of a bulk alloy followed by formation of dispersed Ni particles catalyzing the growth of nitrogen-doped carbon nanofibers was found to take place at temperatures above 560 °C. The final content of nitrogen in obtained carbon nanofibers was about 10 at.%.
Режим доступа: по договору с организацией-держателем ресурса
Argitaratua: 2017
Gaiak:
Sarrera elektronikoa:https://doi.org/10.1016/j.cplett.2017.07.073
Formatua: Baliabide elektronikoa Liburu kapitulua
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=657700