Study of crack resistance of TiAlN coatings by scratch testing

Study of crack resistance of TiAlN coatings by scratch testing

Bibliographic Details
Parent link:	Physical Mesomechanics Vol. 20, iss. 2.— 2017.— [P. 185–192]
Other Authors:	Shugurov A. R. Artur Rubinovich, Akulinkin A. A. Aleksandr Aleksandrovich, Panin A. V. Alexey Viktorovich, Sergeev V. P. Viktor Petrovich, Kalashnikov M. P. Mark Petrovich, Voronov A. V. Andrey Viktorovich, Cheng Chin-Hsiang
Summary:	Title screen Scratch tests were performed to study failure mechanisms in TiAlN coatings deposited on substrates from steel 12Cr18Ni9Ti. It is shown that coating failure begins with crack generation at the apices of pile-ups formed along the scratch due to plastic ploughing of the substrate material. With further increase in indentation load the failure process is governed by the competition between tensile stresses behind the indenter arising due to friction force and stresses at the contact area periphery due to coating bending under normal load. Substrate pretreatment by Ti ion beams is shown to simultaneously increase the hardness and crack resistance of TiAlN coatings. Режим доступа: по договору с организацией-держателем ресурса
Published:	2017
Subjects:	труды учёных ТПУ электронный ресурс тестеры трещиностойкость деформации разрушение кривизна поверхности твердые покрытия scratch testing crack resistance deformation and failure local surface curvature hard coatings
Online Access:	https://doi.org/10.1134/S1029959917020084