Microstructural Aspects of Corrosion; Journal of Surface Investigation. X-ray, Synchrotron and Neutron Techniques; Vol. 14, iss. 6
| Parent link: | Journal of Surface Investigation. X-ray, Synchrotron and Neutron Techniques Vol. 14, iss. 6.— 2020.— [P. 1316-1323] |
|---|---|
| Ente Autore: | |
| Altri autori: | , , , , , |
| Riassunto: | Title screen The effect of metal corrosion on the third-order microscopic properties, i.e., the root-mean-square deviation and internal residual stresses of the first-order, was studied. The corrosion process was studied on steel specimens under conditions of superheated steam (250°C) during 500 h. The X-ray diffraction method was taken as the basic research method. The process of corrosion failure was concluded to have two reproducible periods: the period of active metal dissolution and latent passivation period, followed by the corrosion initiation phase. The metal passivity occurs due to the compressive stresses. Режим доступа: по договору с организацией-держателем ресурса |
| Lingua: | inglese |
| Pubblicazione: |
2020
|
| Soggetti: | |
| Accesso online: | https://doi.org/10.1134/S1027451020060361 |
| Natura: | Elettronico Capitolo di libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=657224 |
| Riassunto: | Title screen The effect of metal corrosion on the third-order microscopic properties, i.e., the root-mean-square deviation and internal residual stresses of the first-order, was studied. The corrosion process was studied on steel specimens under conditions of superheated steam (250°C) during 500 h. The X-ray diffraction method was taken as the basic research method. The process of corrosion failure was concluded to have two reproducible periods: the period of active metal dissolution and latent passivation period, followed by the corrosion initiation phase. The metal passivity occurs due to the compressive stresses. Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| DOI: | 10.1134/S1027451020060361 |