Microstructural Aspects of Corrosion

Microstructural Aspects of Corrosion

Bibliographic Details
Parent link:	Journal of Surface Investigation. X-ray, Synchrotron and Neutron Techniques Vol. 14, iss. 6.— 2020.— [P. 1316-1323]
Corporate Author:	Национальный исследовательский Томский политехнический университет Инженерная школа энергетики Научно-образовательный центр И. Н. Бутакова (НОЦ И. Н. Бутакова)
Other Authors:	Lyubimova L. L. Lyudmila Leonidovna, Buvakov K. V. Konstantin Vladimirovich, Fisenko R. N. Roman Nikolaevich, Zavorin A. S. Aleksandr Sergeevich, Tashlykov A. A. Aleksandr Anatolievich, Shmitov D. M. Denis Maksimovich
Summary:	Title screen The effect of metal corrosion on the third-order microscopic properties, i.e., the root-mean-square deviation and internal residual stresses of the first-order, was studied. The corrosion process was studied on steel specimens under conditions of superheated steam (250°C) during 500 h. The X-ray diffraction method was taken as the basic research method. The process of corrosion failure was concluded to have two reproducible periods: the period of active metal dissolution and latent passivation period, followed by the corrosion initiation phase. The metal passivity occurs due to the compressive stresses. Режим доступа: по договору с организацией-держателем ресурса
Published:	2020
Subjects:	электронный ресурс труды учёных ТПУ low alloy steel modelling studies weight loss X-ray diffraction passivity stress corrosion низколегированные стали модельные исследования дифракция рентгеновские лучи пассивность коррозия
Online Access:	https://doi.org/10.1134/S1027451020060361
Format:	Electronic Book Chapter
KOHA link:	https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=657224

Internet

https://doi.org/10.1134/S1027451020060361