Influence of Thermomechanical Treatments on Mechanical Properties and Fracture Mechanism of High-Nitrogen Austenitic Steel
| Parent link: | AIP Conference Proceedings Vol. 1909 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2017 (AMHS’17).— 2017.— [020143, 5 p.] |
|---|---|
| Corporate Author: | |
| Other Authors: | , , , , , , |
| Summary: | Title screen In this paper, the mechanical properties and fracture mechanisms of the high-nitrogen austenitic steel Fe-17Cr-10Mn-7Ni-0.95V-0.8N-0.1C (in wt %) processed by different thermomechanical treatments are investigated. Cold rolling and short-time solid solution hardening contribute to the formation of a rather homogeneous fine-grained structures in the steel, which possess high strength, sufficient plasticity and exhibit excellent product of strength and elongation ([sigma][YS]=540-570 MPa, [sigma][UTS]=900-950 MPa, EL=37%, PSE=33-35 GPa %) in comparison with coldrolled specimens possessing high strength properties, but extremely low elongation ([sigma][YS]=1200 MPa, [sigma][UTS]=1650 MPa, EL=1%, PSE=7 GPa %). Режим доступа: по договору с организацией-держателем ресурса |
| Published: |
2017
|
| Subjects: | |
| Online Access: | https://doi.org/10.1063/1.5013824 |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=657156 |