Structural-phase analysis of sintered alloy WC-30% steel 110G13

Chi tiết về thư mục
Parent link:	Russian Physics Journal Vol. 36, iss. 5.— 1993.— [P. 497-500]
Tác giả khác:	Ivanov Yu. F. Yuriy Fedorovich, Paul A. V., Gnyusov S. F. Sergey Fedorovich, Kulkov S. N. Sergey Nikolaevich, Kozlov E. V.
Tóm tắt:	Title screen Electron diffraction microscopy and x-ray diffraction analysis are used to study the phase composition and structure of hard alloy WC-steel 110G13 immediately after sintering and additional heat treatment. It is shown that quenching in water from 1370 K leads to disappearance of the excess phases and the formation of a less defective and more uniform structure. Режим доступа: по договору с организацией-держателем ресурса
Ngôn ngữ:	Tiếng Anh
Được phát hành:	1993
Những chủ đề:	электронный ресурс труды учёных ТПУ структурно-фазовый анализ сплавы сталь
Truy cập trực tuyến:	https://link.springer.com/article/10.1007/BF00560431
Định dạng:	Điện tử Chương của sách
KOHA link:	https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=655826

Internet