Hydrogen sorption by Ni-coated titanium alloy VT1-0

Бібліографічні деталі
Parent link:International Journal of Hydrogen Energy
Vol. 42, iss. 22.— 2017.— [P. 10604-10610]
Інші автори: Kudiyarov V. N. Victor Nikolaevich, Kashkarov E. B. Egor Borisovich, Syrtanov M. S. Maksim Sergeevich, Lider A. M. Andrey Markovich
Резюме:Title screen
Sorption properties of titanium alloy VT1-0 coated by nickel layer using dc magnetron sputtering were investigated in this paper. The crystalline structure of the coating as well as evaluation of its thickness was analyzed by X-ray diffraction in grazing incidence geometry. It was revealed that the nickel coating significantly increases the hydrogen sorption rate of titanium alloy compared to pure titanium covered with its original oxide layer. Hydrogen sorption rate reduces approximately from 10−3 to 10−4 wt.%/s with increasing the nickel thickness from 1 to 2.6 μm, respectively. Hydrogen sorption kinetics strongly depends on the hydrogenation parameters. The increase of both temperature in the range of 350-550 °C and hydrogen pressure from 1 to 2 atm leads to increase of hydrogen sorption rate.
Режим доступа: по договору с организацией-держателем ресурса
Мова:Англійська
Опубліковано: 2017
Предмети:
Онлайн доступ:https://doi.org/10.1016/j.ijhydene.2017.02.036
Формат: Електронний ресурс Частина з книги
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=655744