Effects of transient thermal shock loadings on the structure of zirconia ceramics
| Parent link: | IOP Conference Series: Materials Science and Engineering Vol. 156 : Materials and Technologies of New Generations in Modern Materials Science.— 2016.— [012029, 5 p.] |
|---|---|
| Main Author: | |
| Corporate Author: | |
| Other Authors: | , |
| Summary: | Title screen In this paper the influence of thermal shock loadings on the phase composition and microstructure of ZrO[2](Y[2]O[3]) and ZrO[2](MgO) ceramics was studied. It was found that thermal shock strains were no effect on phase composition of ZrO[2](Y[2]O[3]) ceramics. Reducing the concentration of high-temperature tetragonal t-ZrO[2] and cubic c-ZrO[2] modifications and rising the content of low-temperature monoclinic m-ZrO[2] crystal system with increasing the number of thermal shock strains were observed. The values of region coherent X-ray scattering of ZrO[2](Y[2]O[3]) ceramics didn't changed, while the crystallite size of ZrO[2](MgO) ceramics decreased. The formation of block structure in all studied ceramics was observed, the sizes of the blocks formed in the ZrO[2](Y[2]O[3]) and ZrO[2](MgO) ceramics were slightly different. The formation of the blocks in ZrO[2](Y[2]O[3]) ceramics occurred on the grain boundaries, while the crystallites in ZrO[2](MgO) ceramics were crushed due to phase transformation. |
| Published: |
2016
|
| Subjects: | |
| Online Access: | http://dx.doi.org/10.1088/1757-899X/156/1/012029 http://earchive.tpu.ru/handle/11683/36539 |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=651462 |