Synthesis and Properties of Iron-Based Magnetic Nanoparticles; Key Engineering Materials; Vol. 712 : Advanced Materials for Technical and Medical Purpose (AMTMP 2016)
| Parent link: | Key Engineering Materials: Scientific Journal Vol. 712 : Advanced Materials for Technical and Medical Purpose (AMTMP 2016).— 2016.— [P. 282-287] |
|---|---|
| Tác giả chính: | |
| Tác giả của công ty: | |
| Tác giả khác: | , |
| Tóm tắt: | Title screen We have obtained magnetite nanoparticles (MNP) by using chemical coprecipitation of Fe{2+} and Fe{3+} in water solution. The size of these particles was less than 9 nm, and they possessed corresponding physical and chemical properties. Citric acid was used to stabilize magnetite particles suspension. The acid was affixed to the surface of the particles by adding it in fresh MNP solution during synthesis. Affixing carboxyl groups on the surface of MNP not only does improve particles' dispersion in solvent, but also allows adding further modifications to their surface. The properties of the particles' microstructure and morphology were determined with X-Ray diffraction (XRD) and transmission electron microscopy (TEM), whereas their magnetic properties were determined by means of automated pulse magnetic field analysis equipment. Magnetic measurements have shown that saturation magnetization was 94 emu/g with nanoparticles being at room temperature. We have also researched possible application of these particles as drug carriers by determining doxorubicin sorption capacity on the surface of MNPs. These MNPs have proven to have perspective ability to be a magnetic field-controlled carrier for cancer-treating drugs. The obtained particles can also potentially be used as a contrast medium for MRI. Режим доступа: по договору с организацией-держателем ресурса |
| Ngôn ngữ: | Tiếng Anh |
| Được phát hành: |
2016
|
| Loạt: | Materials and Technologies for Biomedical Application and Environmental Engineering |
| Những chủ đề: | |
| Truy cập trực tuyến: | http://dx.doi.org/10.4028/www.scientific.net/KEM.712.282 |
| Định dạng: | Điện tử Chương của sách |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=651346 |
MARC
| LEADER | 00000nla2a2200000 4500 | ||
|---|---|---|---|
| 001 | 651346 | ||
| 005 | 20231219112216.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\16595 | ||
| 035 | |a RU\TPU\network\16592 | ||
| 090 | |a 651346 | ||
| 100 | |a 20161109a2016 k y0engy50 ba | ||
| 101 | 0 | |a eng | |
| 105 | |a y z 100zy | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Synthesis and Properties of Iron-Based Magnetic Nanoparticles |f N. Sashko, E. A. Vaytulevich (Vaitulevich), T. A. Yurmazova | |
| 203 | |a Text |c electronic | ||
| 225 | 1 | |a Materials and Technologies for Biomedical Application and Environmental Engineering | |
| 300 | |a Title screen | ||
| 330 | |a We have obtained magnetite nanoparticles (MNP) by using chemical coprecipitation of Fe{2+} and Fe{3+} in water solution. The size of these particles was less than 9 nm, and they possessed corresponding physical and chemical properties. Citric acid was used to stabilize magnetite particles suspension. The acid was affixed to the surface of the particles by adding it in fresh MNP solution during synthesis. Affixing carboxyl groups on the surface of MNP not only does improve particles' dispersion in solvent, but also allows adding further modifications to their surface. The properties of the particles' microstructure and morphology were determined with X-Ray diffraction (XRD) and transmission electron microscopy (TEM), whereas their magnetic properties were determined by means of automated pulse magnetic field analysis equipment. Magnetic measurements have shown that saturation magnetization was 94 emu/g with nanoparticles being at room temperature. We have also researched possible application of these particles as drug carriers by determining doxorubicin sorption capacity on the surface of MNPs. These MNPs have proven to have perspective ability to be a magnetic field-controlled carrier for cancer-treating drugs. The obtained particles can also potentially be used as a contrast medium for MRI. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | 0 | |0 (RuTPU)RU\TPU\network\11477 |t Key Engineering Materials |o Scientific Journal | |
| 463 | 0 | |0 (RuTPU)RU\TPU\network\16425 |t Vol. 712 : Advanced Materials for Technical and Medical Purpose (AMTMP 2016) |o The Workshop , February 15-17, 2016, Tomsk, Russia |o [proceedings] |f National Research Tomsk Polytechnic University (TPU) ; eds. G. E. Osokin [et al.] |v [P. 282-287] |d 2016 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a синтез | |
| 610 | 1 | |a свойства | |
| 610 | 1 | |a железо | |
| 610 | 1 | |a магнитные наночастицы | |
| 610 | 1 | |a лимонная кислота | |
| 610 | 1 | |a изотермы | |
| 610 | 1 | |a оксид железа | |
| 610 | 1 | |a магнетиты | |
| 610 | 1 | |a намагниченность | |
| 700 | 1 | |a Sashko |b N. |g Nikita | |
| 701 | 1 | |a Vaytulevich (Vaitulevich) |b E. A. |c chemist |c Associate Professor of Tomsk Polytechnic University, Candidate of Chemical Sciences |f 1967- |g Elena Anatolievna |3 (RuTPU)RU\TPU\pers\34130 |9 17670 | |
| 701 | 1 | |a Yurmazova |b T. A. |c Chemist |c Associate Professor of Tomsk Polytechnic University, Candidate of chemical Sciences |f 1950- |g Tatyana Aleksandrovna |3 (RuTPU)RU\TPU\pers\33294 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт физики высоких технологий (ИФВТ) |b Кафедра общей химии и химической технологии (ОХХТ) |3 (RuTPU)RU\TPU\col\21253 |
| 801 | 2 | |a RU |b 63413507 |c 20170120 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.4028/www.scientific.net/KEM.712.282 | |
| 942 | |c CF | ||