Fabrication of the Ni[3]Al-based alloy formed by spark plasma sintering of VKNA powders
| Parent link: | IOP Conference Series: Materials Science and Engineering Vol. 124 : Mechanical Engineering, Automation and Control Systems (MEACS2015).— 2016.— [012113, 6 p.] |
|---|---|
| Corporate Authors: | , |
| Other Authors: | , , , |
| Summary: | Title screen The material based on Ni[3]Al intermetallic has been obtained from the industrial powder of a VKNA type by the method of spark plasma sintering. Materials sintering was conducted at the temperature of 1100 °С, compacting pressure of 20 MPa, and during soaking time equal to 5 minutes. The heating rate of samples amounted to 50 and 200 °С/min. It has been established that the material obtained by sintering at the rate of 50 °С/min possesses a maximum value of density (5.93 g/cm{3}) and a maximum level of bending strength (~ 400 MPa). |
| Published: |
2016
|
| Series: | Materials Science in Mechanical Engineering |
| Subjects: | |
| Online Access: | http://dx.doi.org/10.1088/1757-899X/124/1/012113 http://earchive.tpu.ru/handle/11683/33875 |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=648579 |