In-vitro investigation of magnetron-sputtered coatings based on silicon-substituted hydroxyapatite
| Parent link: | Journal of Surface Investigation. X-ray, Synchrotron and Neutron Techniques: Scientific Journal Vol. 5, iss. 6.— 2011.— [P. 1202-1207] |
|---|---|
| Other Authors: | , , , , |
| Summary: | Title screen Silicon-containing calcium phosphate (Si-CaP) coatings on titanium and austenite steel substrates have been prepared by method of high-frequency magnetron sputtering. The powder of silicon-containing hydroxyapatite Ca 10(PO 4) 6 - x(SiO 4) x(HO) 2 - x (Si-HA), where x = 0. 5 obtained using a mechanochemical technique, was used as a target material. The obtained coatings were X-ray amorphous; the elemental composition of the coatings depended on the composition of the target to be sputtered. The coatings were heated in air for 3 hours to the temperature 700°C with the aim of changing their structure. The bioactivity of the coatings was studied using in-vitro tests. The solution of the simulated body fluid (SBF) oversaturated with respect to HA was used as a model medium. The phase elemental composition and morphology of the deposited and annealed Si-CaP coatings before and after submersion into the solution were controlled using the methods of X-ray diffraction (XRD), energy-dispersive X-ray analysis (EDAX), and scanning electron microscopy (SEM). According to the XFA and IR-spectroscopy data, heat treatment in the air yields the formation of an apatite-like phase in the coating. Thermostating of "metal + coating" specimens in the solution of simulated body fluid revealed that all obtained coatings were biologically active, and a calcium phosphate layer was formed on the coating surface during mineralization. The annealed coatings show a higher chemical stability under physiological conditions as compared to amorphous coatings. Режим доступа: по договору с организацией-держателем ресурса |
| Published: |
2011
|
| Subjects: | |
| Online Access: | http://dx.doi.org/10.1134/S1027451011120135 |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=646252 |