Surface hardening of stainless steel by runaway electronspreionized diffuse discharge in air atmosphere
| Parent link: | Journal of Physics: Conference Series Vol. 652 : Gas Discharge Plasmas and Their Applications (GDP 2015).— 2015.— [012039, 5 p.] |
|---|---|
| Drugi avtorji: | , , , |
| Izvleček: | Title screen In this paper we present microhardness measurements of stainless steel surface treated by diffuse discharge in air atmosphere. The cleaning from carbon in comparison to the initial sample was observed at a depth exceeding 20 nm. The oxygen concentration was also increased in comparison to that in the initial sample at a depth of up to about 50 nm. Comparative analysis shows that after treatment the microhardness of stainless steel surface increased in 2 times due to interaction of near-surface layers with product of plasma chemical reactions produced in diffuse discharge. Режим доступа: по договору с организацией-держателем ресурса |
| Jezik: | angleščina |
| Izdano: |
2015
|
| Teme: | |
| Online dostop: | http://dx.doi.org/10.1088/1742-6596/652/1/012039 http://earchive.tpu.ru/handle/11683/18222 |
| Format: | Elektronski Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=644614 |