Влияние ионного азотирования на структуру, прочностные свойства и механизм разрушения аустенитной стали 01Х17Н13М3 с зеренно-субзеренной структурой разной морфологии; Материалы и технологии новых поколений в современном материаловедении
| Parent link: | Материалы и технологии новых поколений в современном материаловедении.— 2016.— [С. 123-126] |
|---|---|
| Tác giả chính: | |
| Tác giả của công ty: | |
| Tác giả khác: | , |
| Tóm tắt: | Заглавие с титульного экрана We studied structure, strength properties and fracture mechanism of austenitic stainless steel after thermomechanical treatments of two regimes, and further low-temperature ion nitriding. Thermomechanical treatments contributed to the formation of grain-(sub) grain structure of submicron scale in the steel containing high density of defects - the grain boundaries, dislocations and (sub)grain boundaries. Ion nitriding contributed to the formation of hardened surface layer with a microhardness of 11-12 GPa. Formation of grain-(sub)grain structure of submicron scale led to the formation of a brittle surface layers - thick nitride layer and zone of internal nitriding (solid solution hardening) in steel. |
| Ngôn ngữ: | Tiếng Nga |
| Được phát hành: |
2016
|
| Loạt: | Поверхностное упрочнение и защитные покрытия |
| Những chủ đề: | |
| Truy cập trực tuyến: | http://earchive.tpu.ru/handle/11683/30999 |
| Định dạng: | Điện tử Chương của sách |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=619076 |