Влияние наноструктурирования поверхностных слоев на усталостную долговечность конструкционной стали 09Г2С
| Parent link: | Материалы и технологии новых поколений в современном материаловедении: сборник трудов Международной конференции с элементами научной школы для молодежи, г. Томск, 9 – 11 ноября 2015 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; Академия наук СССР (АН СССР), Сибирское отделение (СО), Институт физики прочности и материаловедения (ИФПМ) ; Российский фонд фундаментальных исследований (РФФИ). [С. 64-68].— , 2015 |
|---|---|
| Tác giả chính: | |
| Tác giả của công ty: | |
| Tác giả khác: | , |
| Tóm tắt: | Заглавие с титульного экрана This paper presents the results of the effect of different combinations of heat treatment and nanostructuring of the surface layers on the fatigue life of 09G2S steel. One of the most important scientific and technical problems of our time is the problem of extending the life of the safe operation of potentially dangerous high-risk facilities, without accidents and pollution. These systems include the main gas pipelines of the increased risk of them technological accidents caused by lack of operational reliability of the metal. Conducted fatigue tests have shown the effectiveness of the use of ultrasonic mechanical forging surface layers of 09G2S steel. Fatigue strength of 09G2S steel with nanostructured surface layer is greater than 80,000 cycles, which is 3.4 times the fatigue life of the quenched samples without nanostructured surface layer, while maintaining the high thermal stability of the nanostructure. Therefore, the formation of the nanostructured surface layer of the structural steel increase cracks initiation voltage. |
| Ngôn ngữ: | Tiếng Nga |
| Được phát hành: |
2015
|
| Loạt: | Проблемы прочности современных конструкционных материалов |
| Những chủ đề: | |
| Truy cập trực tuyến: | http://earchive.tpu.ru/handle/11683/18245 http://www.lib.tpu.ru/fulltext/c/2015/C39/014.pdf |
| Định dạng: | Điện tử Chương của sách |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=616393 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 616393 | ||
| 005 | 20231101132915.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\14631 | ||
| 035 | |a RU\TPU\conf\14630 | ||
| 090 | |a 616393 | ||
| 100 | |a 20151224d2015 k y0rusy50 ca | ||
| 101 | 0 | |a rus |d eng | |
| 102 | |a RU | ||
| 105 | |a y z 101zy | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Влияние наноструктурирования поверхностных слоев на усталостную долговечность конструкционной стали 09Г2С |d Influence of surface layers on nanostructuring fatigue properties of 09G2С structural steel |f А. С. Смирнова, Ю. И. Почивалов, В. Е. Панин | |
| 203 | |a Текст |c электронный | ||
| 225 | 1 | |a Проблемы прочности современных конструкционных материалов | |
| 230 | |a 1 компьютерный файл (pdf; 433 Кб) | ||
| 300 | |a Заглавие с титульного экрана | ||
| 320 | |a [Библиогр.: с. 67-68 (6 назв.)] | ||
| 330 | |a This paper presents the results of the effect of different combinations of heat treatment and nanostructuring of the surface layers on the fatigue life of 09G2S steel. One of the most important scientific and technical problems of our time is the problem of extending the life of the safe operation of potentially dangerous high-risk facilities, without accidents and pollution. These systems include the main gas pipelines of the increased risk of them technological accidents caused by lack of operational reliability of the metal. Conducted fatigue tests have shown the effectiveness of the use of ultrasonic mechanical forging surface layers of 09G2S steel. Fatigue strength of 09G2S steel with nanostructured surface layer is greater than 80,000 cycles, which is 3.4 times the fatigue life of the quenched samples without nanostructured surface layer, while maintaining the high thermal stability of the nanostructure. Therefore, the formation of the nanostructured surface layer of the structural steel increase cracks initiation voltage. | ||
| 337 | |a Adobe Reader | ||
| 463 | 0 | |0 (RuTPU)RU\TPU\conf\14276 |t Материалы и технологии новых поколений в современном материаловедении |o сборник трудов Международной конференции с элементами научной школы для молодежи, г. Томск, 9 – 11 ноября 2015 г. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; Академия наук СССР (АН СССР), Сибирское отделение (СО), Институт физики прочности и материаловедения (ИФПМ) ; Российский фонд фундаментальных исследований (РФФИ) |v [С. 64-68] |d 2015 | |
| 510 | 1 | |a Influence of surface layers on nanostructuring fatigue properties of 09G2С structural steel |z eng | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a наноструктурирование | |
| 610 | 1 | |a поверхностные слои | |
| 610 | 1 | |a усталостная долговечность | |
| 610 | 1 | |a конструкционные стали | |
| 700 | 1 | |a Смирнова |b А. С. | |
| 701 | 1 | |a Почивалов |b Ю. И. | |
| 701 | 1 | |a Панин |b В. Е. |c специалист в области физики и механики деформируемого твердого тела, физического материаловедения |c профессор Томского политехнического университета, доктор физико-математических наук |c заведующий кафедрой материаловедения в машиностроении |c директор Российского материаловедческого центра |c научный руководитель Института физики прочности и материаловедения СО РАН |f 1930- |g Виктор Евгеньевич |2 stltpush |3 (RuTPU)RU\TPU\pers\12102 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт физики высоких технологий (ИФВТ) |b Кафедра материаловедения в машиностроении (ММС) |h 74 |2 stltpush |3 (RuTPU)RU\TPU\col\18688 |
| 801 | 2 | |a RU |b 63413507 |c 20210209 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/18245 | |
| 856 | 4 | |u http://www.lib.tpu.ru/fulltext/c/2015/C39/014.pdf | |
| 942 | |c BK | ||