Thermal characteristics of polymer composites based on epoxy resin and copper nanopowders; International Conference on Thermal Analysis and Calorimetry in Russia (RTAC-2016); Vol. 1
| Parent link: | International Conference on Thermal Analysis and Calorimetry in Russia (RTAC-2016): 16-23 September, 2016 Saint-Petersburg, Russia : proceeding.— , 2016 Vol. 1.— 2016.— P. 724-728 |
|---|---|
| निगमित लेखक: | |
| अन्य लेखक: | , , , |
| सारांश: | The thermal properties of the epoxy composites at the heating to 900°C in the atmosphere of air were characterized using thermogravimetric analysis and differential scanning calorimetry. The epoxy composites were synthesized from epoxy resin ED-20, polyethylene polyamine as curing agent, copper nanopowders and boric acid as filler. The results showed that copper nanopowders catalyzed thermal oxidative degradation of the epoxy composites. The effect of the addition of boric acid in the copper filled epoxy polymer on the thermal behavior of the composite at the heating was studied. It was found that adding boric acid inhibited the degradation process. Представлены результаты термогравиметрического анализа и дифференциальной сканирующей калориметрии эпоксидных композитов при нагревании до 900°С в атмосфере воздуха. Эпоксидные композиты были изготовлены на основе эпоксидной смолы ЭД-20, отвердителя полиэтиленполиамина, нанопорошка меди и борной кислоты в качестве наполнителя. Результаты анализа показали, что нанопорошок меди катализирует термоокислительную деструкцию композитов. Исследование влияния комбинации нанопорошка меди и борной кислоты на термические характеристики композита при нагревании показало, что добавление борной кислоты замедляет процесс термоокислительной деструкции эпоксидных композитов. В фонде НТБ ТПУ отсутствует |
| भाषा: | रूसी |
| प्रकाशित: |
2016
|
| श्रृंखला: | Section 2: Thermal analysis and calorimetry of organic substances and materials |
| विषय: | |
| स्वरूप: | MixedMaterials पुस्तक अध्याय |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=602784 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 602784 | ||
| 005 | 20250916164044.0 | ||
| 035 | |a (RuTPU)RU\TPU\tpu\29367 | ||
| 090 | |a 602784 | ||
| 100 | |a 20171031d2016 k||y0rusy50 ba | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 200 | 1 | |a Thermal characteristics of polymer composites based on epoxy resin and copper nanopowders |f O. B. Nazarenko [et al.] |d Термические характеристики полимерных композитов на основе эпоксидной смолы и нанопорошков меди | |
| 225 | 1 | |a Section 2: Thermal analysis and calorimetry of organic substances and materials | |
| 320 | |a References: p. 727-728 (6 tit.) | ||
| 330 | |a The thermal properties of the epoxy composites at the heating to 900°C in the atmosphere of air were characterized using thermogravimetric analysis and differential scanning calorimetry. The epoxy composites were synthesized from epoxy resin ED-20, polyethylene polyamine as curing agent, copper nanopowders and boric acid as filler. The results showed that copper nanopowders catalyzed thermal oxidative degradation of the epoxy composites. The effect of the addition of boric acid in the copper filled epoxy polymer on the thermal behavior of the composite at the heating was studied. It was found that adding boric acid inhibited the degradation process. | ||
| 330 | |a Представлены результаты термогравиметрического анализа и дифференциальной сканирующей калориметрии эпоксидных композитов при нагревании до 900°С в атмосфере воздуха. Эпоксидные композиты были изготовлены на основе эпоксидной смолы ЭД-20, отвердителя полиэтиленполиамина, нанопорошка меди и борной кислоты в качестве наполнителя. Результаты анализа показали, что нанопорошок меди катализирует термоокислительную деструкцию композитов. Исследование влияния комбинации нанопорошка меди и борной кислоты на термические характеристики композита при нагревании показало, что добавление борной кислоты замедляет процесс термоокислительной деструкции эпоксидных композитов. | ||
| 333 | |a В фонде НТБ ТПУ отсутствует | ||
| 461 | 1 | |t International Conference on Thermal Analysis and Calorimetry in Russia (RTAC-2016) |o 16-23 September, 2016 Saint-Petersburg, Russia : proceeding |d 2016 | |
| 463 | 1 | |t Vol. 1 |v P. 724-728 |d 2016 | |
| 510 | 1 | |a Термические характеристики полимерных композитов на основе эпоксидной смолы и нанопорошков меди |z rus | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a полимерные композиты | |
| 610 | 1 | |a эпоксидные смолы | |
| 610 | 1 | |a медь | |
| 610 | 1 | |a нанопорошки | |
| 701 | 1 | |a Nazarenko |b O. B. |c Specialist in the field of ecology and life safety |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1963- |g Olga Bronislavovna |3 (RuTPU)RU\TPU\pers\31918 |9 15988 | |
| 701 | 1 | |a Sechin |b A. I. |c Specialist in the field of ecology and life safety |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1950- |g Aleksandr Ivanovich |3 (RuTPU)RU\TPU\pers\32037 |9 16084 | |
| 701 | 1 | |a Melnikova |b T. V. |g Tatjyana Vyacheslavovna | |
| 701 | 1 | |a Putkhenpurakalchira |b M. V. |c specialist in the field of ecology and life safety from India |c Associate Scientist of Tomsk Polytechnic University |f 1984- |g Maniyan Visakkh |3 (RuTPU)RU\TPU\pers\36797 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт неразрушающего контроля (ИНК) |b Кафедра экологии и безопасности жизнедеятельности (ЭБЖ) |3 (RuTPU)RU\TPU\col\18720 |
| 801 | 1 | |a RU |b 63413507 |c 20171031 | |
| 801 | 2 | |a RU |b 63413507 |c 20171031 |g RCR | |
| 942 | |c BK | ||