Thermal characteristics of polymer composites based on epoxy resin and copper nanopowders
| Parent link: | International Conference on Thermal Analysis and Calorimetry in Russia (RTAC-2016): 16-23 September, 2016 Saint-Petersburg, Russia : proceeding.— , 2016 Vol. 1.— 2016.— P. 724-728 |
|---|---|
| Altres autors: | , , , |
| Sumari: | The thermal properties of the epoxy composites at the heating to 900°C in the atmosphere of air were characterized using thermogravimetric analysis and differential scanning calorimetry. The epoxy composites were synthesized from epoxy resin ED-20, polyethylene polyamine as curing agent, copper nanopowders and boric acid as filler. The results showed that copper nanopowders catalyzed thermal oxidative degradation of the epoxy composites. The effect of the addition of boric acid in the copper filled epoxy polymer on the thermal behavior of the composite at the heating was studied. It was found that adding boric acid inhibited the degradation process. Представлены результаты термогравиметрического анализа и дифференциальной сканирующей калориметрии эпоксидных композитов при нагревании до 900°С в атмосфере воздуха. Эпоксидные композиты были изготовлены на основе эпоксидной смолы ЭД-20, отвердителя полиэтиленполиамина, нанопорошка меди и борной кислоты в качестве наполнителя. Результаты анализа показали, что нанопорошок меди катализирует термоокислительную деструкцию композитов. Исследование влияния комбинации нанопорошка меди и борной кислоты на термические характеристики композита при нагревании показало, что добавление борной кислоты замедляет процесс термоокислительной деструкции эпоксидных композитов. В фонде НТБ ТПУ отсутствует |
| Idioma: | rus |
| Publicat: |
2016
|
| Col·lecció: | Section 2: Thermal analysis and calorimetry of organic substances and materials |
| Matèries: | |
| Format: | Capítol de llibre |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=602784 |