Mechanism of local damage to photovoltaic cells by geomagnetic plasma electrons; Technical Physics; Vol. 70, No. 7
| Parent link: | Technical Physics.— .— Saint Petersburg: Ioffe Institute Vol. 70, No. 7.— 2025.— P. 1311-1321 |
|---|---|
| Andre forfattere: | , , , , |
| Summary: | Title screen With regard to the initial period of active existence of a spacecraft (SC), the processes of anomalous degradation of the power of InGaP/InGaAs/Ge photovoltaic cells (PVC) were experimentally studied during bench tests for the effect of geomagnetic plasma by modeling the electron component of the plasma taking into account the periodic intersection of the SC orbit with the Earth's radiation belt, including the auroral zone. Using the methods of video recording of electroluminescence and measuring dark I-V curves under bench conditions, as well as the methods of microscopy, absolute spectrometry of electroluminescence and dark I-V curves after the end of bench tests, the processes of anomalous degradation of PVC were established, occurring with the participation of technological microdefects of the surface and microbreakdowns of the cover glasses of K-208. A phenomenological impact mechanism of anomalous accelerated degradation of the power of PVC at the initial stage of the SC existence is proposed. The highest rate of anomalous power degradation is observed for solar cells with technological defects in p-n-junctions. Keywords: solar panels of spacecraft, geomagnetic plasma, anode-initiated flashover, bulk microbreakdown of dielectric, damage to photovoltaic device Применительно к начальному времени срока активного существования космического аппарата экспериментально исследованы процессы аномальной деградации мощности солнечных InGaP/GaAs/Ge-фотоэлементов при стендовых испытаниях на воздействие геомагнитной плазмы путем моделирования электронной компоненты плазмы с учетом периодического пересечении орбитой космического аппарата радиационного пояса Земли, включая авроральную зону. Методами видеорегистрации электролюминесценции и измерения темновых вольт-амперных характеристик в стендовых условиях, а также методами микроскопии, абсолютной спектрометрии электролюминесценции и темновых вольт-амперных характеристик после окончания стендовых испытаний установлены процессы аномальной деградации фотоэлементов, происходящие с участием технологических микродефектов поверхности и микропробоев покровных стекол К-208. Предложен феноменологический ударный механизм аномальной ускоренной деградации мощности фотоэлементов на начальном этапе существования космического аппарата. Наиболее высокая скорость аномальной деградации мощности наблюдается для фотоэлементов, имеющих технологические дефекты p-n-переходов. Ключевые слова: солнечные батареи космических аппаратов, геомагнитная плазма, анодно-инициируемый поверхностный разряд, объемный микропробой диэлектрика, повреждение фотопреобразователя Текстовый файл |
| Sprog: | engelsk |
| Udgivet: |
2025
|
| Fag: | |
| Online adgang: | https://journals.ioffe.ru/articles/61460 Статья на русском языке |
| Format: | Electronisk Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=686073 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 686073 | ||
| 005 | 20260409153401.0 | ||
| 090 | |a 686073 | ||
| 100 | |a 20260409d2025 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i |b e | |
| 182 | 0 | |a b | |
| 183 | 0 | |a cr |2 RDAcarrier | |
| 200 | 1 | |a Mechanism of local damage to photovoltaic cells by geomagnetic plasma electrons |d Механизм локальных повреждений фотоэлементов электронами геомагнитной плазмы |f Zykov V. M., Evdokimov K. E., Neyman D. A [et al.] |z rus | |
| 203 | |a Текст |c электронный |b визуальный | ||
| 283 | |a online_resource |2 RDAcarrier | ||
| 300 | |a Title screen | ||
| 320 | |a References: 29 tit. | ||
| 330 | |a With regard to the initial period of active existence of a spacecraft (SC), the processes of anomalous degradation of the power of InGaP/InGaAs/Ge photovoltaic cells (PVC) were experimentally studied during bench tests for the effect of geomagnetic plasma by modeling the electron component of the plasma taking into account the periodic intersection of the SC orbit with the Earth's radiation belt, including the auroral zone. Using the methods of video recording of electroluminescence and measuring dark I-V curves under bench conditions, as well as the methods of microscopy, absolute spectrometry of electroluminescence and dark I-V curves after the end of bench tests, the processes of anomalous degradation of PVC were established, occurring with the participation of technological microdefects of the surface and microbreakdowns of the cover glasses of K-208. A phenomenological impact mechanism of anomalous accelerated degradation of the power of PVC at the initial stage of the SC existence is proposed. The highest rate of anomalous power degradation is observed for solar cells with technological defects in p-n-junctions. Keywords: solar panels of spacecraft, geomagnetic plasma, anode-initiated flashover, bulk microbreakdown of dielectric, damage to photovoltaic device | ||
| 330 | |a Применительно к начальному времени срока активного существования космического аппарата экспериментально исследованы процессы аномальной деградации мощности солнечных InGaP/GaAs/Ge-фотоэлементов при стендовых испытаниях на воздействие геомагнитной плазмы путем моделирования электронной компоненты плазмы с учетом периодического пересечении орбитой космического аппарата радиационного пояса Земли, включая авроральную зону. Методами видеорегистрации электролюминесценции и измерения темновых вольт-амперных характеристик в стендовых условиях, а также методами микроскопии, абсолютной спектрометрии электролюминесценции и темновых вольт-амперных характеристик после окончания стендовых испытаний установлены процессы аномальной деградации фотоэлементов, происходящие с участием технологических микродефектов поверхности и микропробоев покровных стекол К-208. Предложен феноменологический ударный механизм аномальной ускоренной деградации мощности фотоэлементов на начальном этапе существования космического аппарата. Наиболее высокая скорость аномальной деградации мощности наблюдается для фотоэлементов, имеющих технологические дефекты p-n-переходов. Ключевые слова: солнечные батареи космических аппаратов, геомагнитная плазма, анодно-инициируемый поверхностный разряд, объемный микропробой диэлектрика, повреждение фотопреобразователя | ||
| 336 | |a Текстовый файл | ||
| 461 | 1 | |t Technical Physics |c Saint Petersburg |n Ioffe Institute | |
| 463 | 1 | |t Vol. 70, No. 7 |v P. 1311-1321 |d 2025 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a solar panels of spacecraft | |
| 610 | 1 | |a geomagnetic plasma | |
| 610 | 1 | |a anode-initiated flashover | |
| 610 | 1 | |a bulk microbreakdown of dielectric | |
| 610 | 1 | |a damage to photovoltaic device | |
| 701 | 1 | |a Zykov |b V. M. |c Physicist, Specialist in the field of quality |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1940- |g Vladimir Mikhailovich |9 20690 | |
| 701 | 1 | |a Evdokimov |b K. E. |c physicist |c Associate Professor of Tomsk Polytechnic University, Candidate of physical and mathematical sciences |f 1976- |g Kirill Evgenievich |9 15902 | |
| 701 | 1 | |a Neyman |b D. A. |c physicist |c Engineer of Tomsk Polytechnic University |f 1989- |g Dmitry Aleksandrovich |9 20911 | |
| 701 | 1 | |a Vladimirov |b A. M. |c Physicist |c Engineer of Tomsk Polytechnic University |f 1988- |g Aleksandr Mikhailovich |9 20689 | |
| 701 | 1 | |a Voronova |b G. A. |c chemist |c Associate Professor of Tomsk Polytechnic University, candidate of chemical sciences |f 1974- |g Gulnara Alfridovna |9 19500 | |
| 801 | 0 | |a RU |b 63413507 |c 20260409 |g RCR | |
| 856 | 4 | 0 | |u https://journals.ioffe.ru/articles/61460 |z https://journals.ioffe.ru/articles/61460 |
| 856 | 4 | 0 | |u https://journals.ioffe.ru/articles/60662 |z Статья на русском языке |
| 942 | |c CF | ||