Cathodoluminescence properties of oxide and fluoride ceramics synthesized in the field of high-energy electrons flux; Вестник Карагандинского университета. Серия Физика; № 4 (116)
| Parent link: | Вестник Карагандинского университета. Серия Физика.— .— Караганда: КарГУ № 4 (116).— 2024.— С. 54-59 |
|---|---|
| Huvudupphovsman: | |
| Övriga upphovsmän: | |
| Sammanfattning: | Traditionally, the synthesis of refractory ceramics is a complex and time-consuming process. Some time ago, a new, much faster method was proposed — the method of synthesis of luminescent ceramics in the field of a powerful flux of high-energy electrons. In the synthesis of multicomponent oxide phosphors, it is not an easy task to determine the dependencies of the properties of the resulting material on the composition of the raw mixture and the modes of the synthesis process. In this regard, it seems logical to study the properties of ce- ramics made by radiation synthesis from simple oxides, which are components of more complex phosphors. An investigation of the spectral and kinetic patterns of cathodoluminescence of ceramic samples of metal ox- ides (Ga2O3, Al2O3, Y2O3) and fluorides (MgF2, BaF2) obtained by radiation synthesis method was carried out. The paper presents an analysis of the cathodoluminescence spectra of the studied samples with the allo- cation of elementary bands, conclusions about the dynamics of luminescence decay are made. The obtained results are compared with the known data on single crystal samples. It is shown that, unlike oxide ceramics, the spectral characteristics of MgF2 and BaF2 ceramic samples show good agreement with the data on single crystals of these compounds Традиционно синтез тугоплавкой керамики является сложным и долгим процессом. Некоторое время назад был предложен новый, намного более быстрый метод — метод синтеза люминесцентной керамики в поле мощного потока высокоэнергетических электронов. Синтез оксидной керамики по принципиально новой технологии требует всестороннего изучения свойств этой керамики. При синтезе многокомпонентных оксидных люминофоров непростой задачей является определение зависимостей свойств получаемого материала от состава исходного сырья, режимов процесса синтеза. Образцы для данной работы были синтезированы путем прямого воздействия на сырье электронного пучка. В работе исследовались закономерности катодолюминесценции образцов керамики оксидов металлов (Ga2O3, Al2O3, Y2O3) и фторидов металлов (MgF2, BaF2), синтезированной радиационным методом. Люминесценция возбуждалась пучком электронов со средней энергией электронов в импульсе 250 кэВ. Для регистрации спектров и кинетик люминесценции использовался метод импульсной спектрометрии с временным разрешением 7 нс. Авторами представлен анализ спектров катодолюминесценции изученных образцов с выделением элементарных полос, сделаны заключения о динамике затухания люминесценции в отдельных полосах. Проведено сравнение полученных результатов с известными данными по монокристаллическим образцам. Показано, что, в отличие от оксидной керамики, спектральные характеристики образцов керамик MgF2, BaF2 показывают хорошее соответствие с данными по монокристаллам этих соединений Текстовый файл |
| Språk: | engelska |
| Publicerad: |
2024
|
| Ämnen: | |
| Länkar: | https://doi.org/10.31489/2024ph4/54-59 |
| Materialtyp: | Elektronisk Bokavsnitt |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=682986 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 682986 | ||
| 005 | 20251111121149.0 | ||
| 090 | |a 682986 | ||
| 100 | |a 20251111d2024 k||y0rusy50 ba | ||
| 101 | 0 | |a eng |c rus | |
| 102 | |a KZ | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i |b e | |
| 182 | 0 | |a b | |
| 183 | 0 | |a cr |2 RDAcarrier | |
| 200 | 1 | |a Cathodoluminescence properties of oxide and fluoride ceramics synthesized in the field of high-energy electrons flux |d Свойства катодолюминесценции оксидной и фторидной керамики, синтезированной в поле потока высокоэнергетических электронов |f А. А. Karnaukhova, V. Y. Yakovlev |z rus | |
| 203 | |a Текст |c электронный |b визуальный | ||
| 283 | |a online_resource |2 RDAcarrier | ||
| 320 | |a References: 4 tit | ||
| 330 | |a Traditionally, the synthesis of refractory ceramics is a complex and time-consuming process. Some time ago, a new, much faster method was proposed — the method of synthesis of luminescent ceramics in the field of a powerful flux of high-energy electrons. In the synthesis of multicomponent oxide phosphors, it is not an easy task to determine the dependencies of the properties of the resulting material on the composition of the raw mixture and the modes of the synthesis process. In this regard, it seems logical to study the properties of ce- ramics made by radiation synthesis from simple oxides, which are components of more complex phosphors. An investigation of the spectral and kinetic patterns of cathodoluminescence of ceramic samples of metal ox- ides (Ga2O3, Al2O3, Y2O3) and fluorides (MgF2, BaF2) obtained by radiation synthesis method was carried out. The paper presents an analysis of the cathodoluminescence spectra of the studied samples with the allo- cation of elementary bands, conclusions about the dynamics of luminescence decay are made. The obtained results are compared with the known data on single crystal samples. It is shown that, unlike oxide ceramics, the spectral characteristics of MgF2 and BaF2 ceramic samples show good agreement with the data on single crystals of these compounds | ||
| 330 | |a Традиционно синтез тугоплавкой керамики является сложным и долгим процессом. Некоторое время назад был предложен новый, намного более быстрый метод — метод синтеза люминесцентной керамики в поле мощного потока высокоэнергетических электронов. Синтез оксидной керамики по принципиально новой технологии требует всестороннего изучения свойств этой керамики. При синтезе многокомпонентных оксидных люминофоров непростой задачей является определение зависимостей свойств получаемого материала от состава исходного сырья, режимов процесса синтеза. Образцы для данной работы были синтезированы путем прямого воздействия на сырье электронного пучка. В работе исследовались закономерности катодолюминесценции образцов керамики оксидов металлов (Ga2O3, Al2O3, Y2O3) и фторидов металлов (MgF2, BaF2), синтезированной радиационным методом. Люминесценция возбуждалась пучком электронов со средней энергией электронов в импульсе 250 кэВ. Для регистрации спектров и кинетик люминесценции использовался метод импульсной спектрометрии с временным разрешением 7 нс. Авторами представлен анализ спектров катодолюминесценции изученных образцов с выделением элементарных полос, сделаны заключения о динамике затухания люминесценции в отдельных полосах. Проведено сравнение полученных результатов с известными данными по монокристаллическим образцам. Показано, что, в отличие от оксидной керамики, спектральные характеристики образцов керамик MgF2, BaF2 показывают хорошее соответствие с данными по монокристаллам этих соединений | ||
| 336 | |a Текстовый файл | ||
| 461 | 1 | |t Вестник Карагандинского университета. Серия Физика |c Караганда |n КарГУ | |
| 463 | 1 | |t № 4 (116) |v С. 54-59 |d 2024 | |
| 610 | 1 | |a oxide ceramics | |
| 610 | 1 | |a fluoride ceramics | |
| 610 | 1 | |a cathodoluminescence | |
| 610 | 1 | |a radiation synthesis | |
| 610 | 1 | |a spectra | |
| 610 | 1 | |a time resolution | |
| 610 | 1 | |a Ga2O3 | |
| 610 | 1 | |a Al2O3 | |
| 610 | 1 | |a Y2O3 | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 700 | 1 | |a Karnaukhova |b A. A. |c specialist in the field of lightning engineering |c Assistant, Associate Professor of Tomsk Polytechnic University |f 1983- |g Anna Alekseevna |9 20534 | |
| 701 | 1 | |a Yakovlev |b V. Yu. |c specialist in the field of lightning engineering |c Professor of Tomsk Polytechnic University, Doctor of physical and mathematical sciences |f 1949- |g Viktor Yurjevich |9 18886 | |
| 801 | 0 | |a RU |b 63413507 |c 20251111 | |
| 856 | 4 | |u https://doi.org/10.31489/2024ph4/54-59 |z https://doi.org/10.31489/2024ph4/54-59 | |
| 942 | |c CF | ||