Исследование пьезо- и магнитоэлектрического отклика наночастиц структуры ядро-оболочка на основе MnFe2O4 и Ba0.85Ca0.15Zr0.1Ti0.9O3; Перспективы развития фундаментальных наук; Т. 1 : Физика
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XХII Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 22-25 апреля 2025/ Национальный исследовательский Томский политехнический университет ; под ред. И. А. Курзиной [и др.].— .— Томск: Изд-во ТПУ Т. 1 : Физика.— 2025.— С. 137-139 |
|---|---|
| Hlavní autor: | |
| Další autoři: | , , |
| Shrnutí: | Заглавие с экрана Herein, the ferroelectric (FE), piezoelectric (PE) and magnetoelectric (ME) behavior of core-shell ME nanoparticles (NP) were studied using piezoresponse force microscopy. These NPs based on a magnetostrictive MnFe2O4 (MFO) core and a ferroelectric Ba0.85Ca0.15Zr0.1Ti0.9O3 (BCZT) shell were fabricated via microwave hydrothermal synthesis. The observed switching of the polarization confirmed the presence of FE properties in MFO@BCZT NPs. The PE response of MFO@BCZT NPs was 9.95 ± 1.36 pm/V, whereas the ME response was 81·104 mV·cm⁻¹·Oe⁻¹. The obtained values are comparable to those of potentially toxic analogues. Thus, these MFO@BCZT NPs can be considered as a new promising platform for non-invasive electrotherapy of neurological disorders and neurotrauma Текстовый файл |
| Jazyk: | ruština |
| Vydáno: |
2025
|
| Témata: | |
| On-line přístup: | http://earchive.tpu.ru/handle/11683/132827 |
| Médium: | MixedMaterials Elektronický zdroj Kapitola |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=682395 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 682395 | ||
| 005 | 20251101142240.0 | ||
| 090 | |a 682395 | ||
| 100 | |a 20251016d2025 k||y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 200 | 1 | |a Исследование пьезо- и магнитоэлектрического отклика наночастиц структуры ядро-оболочка на основе MnFe2O4 и Ba0.85Ca0.15Zr0.1Ti0.9O3 |d Study of the piezoelectric and magnetoelectric response of core-shell nanoparticles based on MnFe2O4 and Ba0.85Ca0.15Zr0.1Ti0.9O3 |f Д. А. Копцев, Р. В. Чернозём, М. А. Сурменева |g науч. рук. Р. А. Сурменев |z eng | |
| 300 | |a Заглавие с экрана | ||
| 320 | |a Список литературы: 8 назв | ||
| 330 | |a Herein, the ferroelectric (FE), piezoelectric (PE) and magnetoelectric (ME) behavior of core-shell ME nanoparticles (NP) were studied using piezoresponse force microscopy. These NPs based on a magnetostrictive MnFe2O4 (MFO) core and a ferroelectric Ba0.85Ca0.15Zr0.1Ti0.9O3 (BCZT) shell were fabricated via microwave hydrothermal synthesis. The observed switching of the polarization confirmed the presence of FE properties in MFO@BCZT NPs. The PE response of MFO@BCZT NPs was 9.95 ± 1.36 pm/V, whereas the ME response was 81·104 mV·cm⁻¹·Oe⁻¹. The obtained values are comparable to those of potentially toxic analogues. Thus, these MFO@BCZT NPs can be considered as a new promising platform for non-invasive electrotherapy of neurological disorders and neurotrauma | ||
| 336 | |a Текстовый файл | ||
| 461 | 1 | |0 682243 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XХII Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 22-25 апреля 2025 |9 682243 |c Томск |n Изд-во ТПУ |f Национальный исследовательский Томский политехнический университет ; под ред. И. А. Курзиной [и др.] | |
| 463 | 1 | |0 682245 |9 682245 |t Т. 1 : Физика |d 2025 |u conference_tpu-2025-C21_V1.pdf |v С. 137-139 |l Vol. 1 : Physics | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a ferroelectrics | |
| 610 | 1 | |a piezoelectrics | |
| 610 | 1 | |a magnetoelectrics | |
| 610 | 1 | |a core-shell nanoparticles | |
| 700 | 1 | |a Копцев |b Д. А. |c специалист в области материаловедения |c лаборант кафедры Томского политехнического университета |f 2003- |g Данила Андреевич |9 22859 | |
| 701 | 1 | |a Чернозем |b Р. В. |c физик |c доцент Томского политехнического университета |f 1992- |g Роман Викторович |9 18423 | |
| 701 | 1 | |a Сурменева |b М. А. |c специалист в области материаловедения |c инженер-исследователь Томского политехнического университета, старший научный сотрудник |f 1984- |g Мария Александровна |9 11705 | |
| 702 | 1 | |a Сурменев |b Р. А. |c физик |c старший научный сотрудник Томского политехнического университета, доцент, кандидат физико-математических наук |f 1982- |g Роман Анатольевич |4 727 | |
| 801 | 0 | |a RU |b 63413507 |c 20251016 |g RCR | |
| 856 | 4 | |z http://earchive.tpu.ru/handle/11683/132827 |u http://earchive.tpu.ru/handle/11683/132827 | |
| 942 | |c CF | ||