Spectral Characteristics of Photoluminescence Synthesized in the Field of Radiation YAGG Phosphors with Different Al/Ga Ratio; Вестник Карагандинского университета. Серия Физика; № 4 (116)
| Parent link: | Вестник Карагандинского университета. Серия Физика=Bulletin of the Karaganda University. Series Physics/ Карагандинский университет имени академика Е. А. Букетова.— .— Караганда: КарГУ.— 2518-7198 № 4 (116).— 2024.— С. 114-122 |
|---|---|
| مؤلفون آخرون: | , , , , |
| الملخص: | In the study the results of luminescence spectra investigating and excitation of ceramics luminescence with different Al/Ga ratios, synthesized by irradiating a mixture of initial materials with different prehistories were presented. Mixtures of oxides powders with stoichiometric composition corresponding to Y3AlxGa5-xO12: Ce, where x ranged from 0 to 5, were prepared for synthesis. All initial materials had a purity of no less than ana- lytical grade. The synthesis was carried out under the influence of an electron beam with an energy of 1.4 MeV and a power density of 20 kW/cm2. The yield of the synthesis reaction, the ratio of the sample mass to the mixture, was 90‒95 %. Research has shown that decreasing the Al/Ga ratio results in a shift of the lu- minescence band towards the short-wavelength region of the spectrum. Additionally, the excitation spectrum changes. As the Al/Ga ratio decreases, the excitation band shifts towards the long-wavelength region around 350 nm. The characteristics of luminescence are influenced by the prehistory of the initial materials В статье представлены результаты исследования спектров люминесценции и возбуждения люминесценции керамики с различным соотношением Al/Ga, синтезированной путем облучения смеси исходных материалов с различной предысторией. Для синтеза были подготовлены смеси порошков оксидов со стехиометрическим составом, соответствующим Y3AlxGa5-xO12: Ce, где x варьируется от 0 до 5. Все исходные материалы имели чистоту не ниже аналитической. Синтез проводился под воздействием электронного пучка с энергией 1,4 МэВ и плотностью мощности 20 кВт/см2. Выход реакции синтеза —отношение массы образца к массе смеси —составил 90–95%. Исследования показали, что уменьшение соотношения Al/Ga приводит к смещению полосы люминесценции в коротковолновую область спектра. Кроме того, изменяется спектр возбуждения. При уменьшении соотношения Al/Ga полоса возбуждения смещается в длинноволновую область около 350 нм. На характеристики люминесценции влияет предыстория исходных материалов Текстовый файл |
| اللغة: | الإنجليزية |
| منشور في: |
2024
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | https://doi.org/10.31489/2024ph4/114-122 |
| التنسيق: | MixedMaterials الكتروني فصل الكتاب |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=678825 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 678825 | ||
| 005 | 20250619154227.0 | ||
| 090 | |a 678825 | ||
| 100 | |a 20250225d2024 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a KZ | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i |b e | |
| 182 | 0 | |a b | |
| 183 | 0 | |a cr |2 RDAcarrier | |
| 200 | 1 | |a Spectral Characteristics of Photoluminescence Synthesized in the Field of Radiation YAGG Phosphors with Different Al/Ga Ratio |d Спектральные характеристики фотолюминесценции синтезированных в поле радиации YAGG люминофоров с различным соотношением Al/Ga |z rus |f A. T. Tulegenova, G. Zh. Nogaibekova, I. A. Saidazimov [et al.] | |
| 203 | |a Текст |c электронный |b визуальный | ||
| 283 | |a online_resource |2 RDAcarrier | ||
| 320 | |a References: 23 tit | ||
| 330 | |a In the study the results of luminescence spectra investigating and excitation of ceramics luminescence with different Al/Ga ratios, synthesized by irradiating a mixture of initial materials with different prehistories were presented. Mixtures of oxides powders with stoichiometric composition corresponding to Y3AlxGa5-xO12: Ce, where x ranged from 0 to 5, were prepared for synthesis. All initial materials had a purity of no less than ana- lytical grade. The synthesis was carried out under the influence of an electron beam with an energy of 1.4 MeV and a power density of 20 kW/cm2. The yield of the synthesis reaction, the ratio of the sample mass to the mixture, was 90‒95 %. Research has shown that decreasing the Al/Ga ratio results in a shift of the lu- minescence band towards the short-wavelength region of the spectrum. Additionally, the excitation spectrum changes. As the Al/Ga ratio decreases, the excitation band shifts towards the long-wavelength region around 350 nm. The characteristics of luminescence are influenced by the prehistory of the initial materials | ||
| 330 | |a В статье представлены результаты исследования спектров люминесценции и возбуждения люминесценции керамики с различным соотношением Al/Ga, синтезированной путем облучения смеси исходных материалов с различной предысторией. Для синтеза были подготовлены смеси порошков оксидов со стехиометрическим составом, соответствующим Y3AlxGa5-xO12: Ce, где x варьируется от 0 до 5. Все исходные материалы имели чистоту не ниже аналитической. Синтез проводился под воздействием электронного пучка с энергией 1,4 МэВ и плотностью мощности 20 кВт/см2. Выход реакции синтеза —отношение массы образца к массе смеси —составил 90–95%. Исследования показали, что уменьшение соотношения Al/Ga приводит к смещению полосы люминесценции в коротковолновую область спектра. Кроме того, изменяется спектр возбуждения. При уменьшении соотношения Al/Ga полоса возбуждения смещается в длинноволновую область около 350 нм. На характеристики люминесценции влияет предыстория исходных материалов | ||
| 336 | |a Текстовый файл | ||
| 461 | 1 | |t Вестник Карагандинского университета. Серия Физика |l Bulletin of the Karaganda University. Series Physics |f Карагандинский университет имени академика Е. А. Букетова |c Караганда |n КарГУ |x 2518-7198 | |
| 463 | 1 | |t № 4 (116) |v С. 114-122 |d 2024 | |
| 610 | 1 | |a Al/Ga ratio | |
| 610 | 1 | |a luminescence | |
| 610 | 1 | |a radiation synthesis | |
| 610 | 1 | |a high-energy electron beam | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 701 | 1 | |a Tulegenova |b A. T. | |
| 701 | 1 | |a Nogaibekova |b G. Zh. | |
| 701 | 1 | |a Saidazimov (Saydazimov) |b I. A. |g Ibrokhimkhon Ayupkhonovich |f 1999- |c physicist |c Engineer of Tomsk Polytechnic University |y Tomsk |7 ca |8 eng |9 88857 | |
| 701 | 1 | |a Vil'chinskaya (Vilchinskaya) |b S. S. |c specialist in the field of laser and light technology |c associate Professor of Tomsk Polytechnic University, candidate of physico-mathematical Sciences |f 1976- |g Svetlana Sergeevna |9 17478 | |
| 701 | 1 | |a Markhabayeva |b A. A. | |
| 801 | 0 | |a RU |b 63413507 |c 20250225 |g RCR | |
| 850 | |a 63413507 | ||
| 856 | 4 | |u https://doi.org/10.31489/2024ph4/114-122 |z https://doi.org/10.31489/2024ph4/114-122 | |
| 942 | |c CF | ||