Influence of Refractory Fillers on the Properties of Ceramics Based on Highly Concentrated Silica Glass Suspensions; Glass and Ceramics; Vol. 81, iss. 1-2
| Parent link: | Glass and Ceramics.— .— New York: Springer Science+Business Media LLC. Vol. 81, iss. 1-2.— 2024.— P. 17-23 |
|---|---|
| Rannpháirtithe: | , , , , |
| Achoimre: | Title screen Refractory and heat-resistant materials with a coarse-grained and large-porous structure were obtained using silica glass suspensions with mullite, spinel, alumina, and quartz fillers. The influence of sintering temperature on the phase composition, structure, porosity, and density of the materials were studied. Although the strength of the ceramics was found to increase in the temperature range 1300 – 1400°C, it decreases at 1500 – 1600°C due to the crystallization of the silica glass. Composites in the silica glass-alumina system were found to have the most stable strength characteristics Текстовый файл AM_Agreement |
| Teanga: | Béarla |
| Foilsithe / Cruthaithe: |
2024
|
| Ábhair: | |
| Rochtain ar líne: | https://doi.org/10.1007/s10717-024-00652-7 |
| Formáid: | Leictreonach Caibidil leabhair |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=677974 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 677974 | ||
| 005 | 20260203144929.0 | ||
| 090 | |a 677974 | ||
| 100 | |a 20241227d2024 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a US | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i |b e | |
| 182 | 0 | |a b | |
| 183 | 0 | |a cr |2 RDAcarrier | |
| 200 | 1 | |a Influence of Refractory Fillers on the Properties of Ceramics Based on Highly Concentrated Silica Glass Suspensions |f S. M. Sharafeev, O. V. Kazmina, A. V. Gubanov [et al.] | |
| 203 | |a Текст |c электронный |b визуальный | ||
| 283 | |a online_resource |2 RDAcarrier | ||
| 300 | |a Title screen | ||
| 320 | |a References: 17 tit | ||
| 330 | |a Refractory and heat-resistant materials with a coarse-grained and large-porous structure were obtained using silica glass suspensions with mullite, spinel, alumina, and quartz fillers. The influence of sintering temperature on the phase composition, structure, porosity, and density of the materials were studied. Although the strength of the ceramics was found to increase in the temperature range 1300 – 1400°C, it decreases at 1500 – 1600°C due to the crystallization of the silica glass. Composites in the silica glass-alumina system were found to have the most stable strength characteristics | ||
| 336 | |a Текстовый файл | ||
| 371 | 0 | |a AM_Agreement | |
| 461 | 1 | |t Glass and Ceramics |c New York |n Springer Science+Business Media LLC. | |
| 463 | 1 | |t Vol. 81, iss. 1-2 |d 2024 |v P. 17-23 | |
| 610 | 1 | |a highly concentrated binder suspensions | |
| 610 | 1 | |a silica glass | |
| 610 | 1 | |a refractory filler | |
| 610 | 1 | |a mullite | |
| 610 | 1 | |a spinel | |
| 610 | 1 | |a quartz | |
| 610 | 1 | |a alumina | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 701 | 1 | |a Sharafeev |b Sh. M. |c chemical engineer |c Engineer of Tomsk Polytechnic University, Candidate of Technical Sciences |f 1994- |g Sharif Mnirovich |9 22455 | |
| 701 | 1 | |a Kazmina |b O. V. |c Chemical Engineer |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1967- |g Olga Viktorovna |9 16846 | |
| 701 | 1 | |a Gubanov |b A. V. |g Aleksandr Valerjevich |f 1985- |c specialist in the field of material science |c Engineer of Tomsk Polytechnic University |9 88816 | |
| 701 | 1 | |a Kutugin |b V. A. |c Chemical Engineer |c Associate Professor of Tomsk Polytechnic University, Candidate of Technical Sciences |f 1983- |g Viktor Aleksandrovich |9 18177 | |
| 701 | 1 | |a Polushin |b G. V. |g Gleb Vladimirovich | |
| 801 | 0 | |a RU |b 63413507 |c 20241227 |g RCR | |
| 856 | 4 | 0 | |u https://doi.org/10.1007/s10717-024-00652-7 |z https://doi.org/10.1007/s10717-024-00652-7 |
| 942 | |c CF | ||