Characterization of YAG:Ce ceramics with graphene oxide
| Parent link: | Вестник Карагандинского университета. Физика/ Карагандинский университет им. Е. А. Букетова.— .— Караганда: КарГУ No 3 (111).— 2023.— С. 151-155 |
|---|---|
| Muut tekijät: | , , , , , , , |
| Yhteenveto: | Yttrium-aluminum garnet (Y3Al5O12) is an optical material that shows great potential due to its favorable light-emitting and mechanical properties, as well as its chemical stability and thermal resistance. It is commonly utilized in laser technology, optical instruments, and solid-state light sources as a result of its activation by transition metal or rare earth element ions. In this work, experiments were carried out on the procedure for compacting samples of luminescent ceramics Y3Al5O12:Ce3+, by single-base pressing followed by sintering. Comprehensive studies of the influence of graphene oxide of variable concentration (x=0.1;0.5; 1 wt.%) on the radiative characteristics of ceramic samples. It was found that the addition of graphene oxide in an amount from 0.1 to 1 wt. % affects the density and luminescent properties of YAG:Ce ceramics. There is a decrease in the value of the density parameter at concentrations of graphene oxide 0.1-1 wt. % before annealing, after annealing, the relative density value increases to ~99 %. The luminescence spectrum when excited by a blue LED chip appears as a wide band in the spectral range 460-750, the nature of which is associated with radiative transitions in the cerium ion. It has been established that the light-emitting characteristics have a downward trend when activated by graphene oxide. The integral luminescence intensity decreases from 27.1 % to 19 % with an increase in the concentration of graphene oxide. Иттрий-алюминиевый гранат (Y3Al5O12) является перспективным оптическим материалом с хорошими светоизлучающими и механическими свойствами, химической стабильностью и термической стойкостью. Материалы на основе иттрий-алюминиевого граната, активированного ионами переходных металлов или редкоземельных элементов, широко используются в лазерной технике, оптическом приборостроении и твердотельных источниках света. В настоящей работе были проведены эксперименты по процедуре компактирования образцов люминесцентной керамики Y3Al5O12:Ce3+, путем одноосновного прессования с последующим спеканием. Проведены комплексные исследования влияния оскида графена переменной концентрации (x=0,1; 0,5; 1 вес. %) на излучательные характеристики образцов керамики. Было установлено, что добавка оксида графена в количестве от 0,1 до 1 мас. % влияет на плотность и люминесцентные свойства YAG:Ce керамики. Наблюдается снижение значения параметра плотности при концентрациях оксида графена 0,1–1 вес. % до отжига, после отжига значение относительной плотности повышается до ~99%. Спектр люминесценции при возбуждении синий, чипом светодиода проявляется в виде широкой полосы в спектральном диапазоне 460–750, природа которой связана с излучательными переходами в ионе церия. Установлено, что светоизлучающие характеристики имеют динамику к снижению при активации оксидом графена. Интегральная интенсивность свечения уменьшается с 27,1до 19% при повышении концентрации оксида графена. Текстовый файл |
| Kieli: | englanti |
| Julkaistu: |
2023
|
| Aiheet: | |
| Linkit: | https://doi.org/10.31489/2023ph3/151-155 |
| Aineistotyyppi: | Elektroninen Kirjan osa |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=676156 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 676156 | ||
| 005 | 20251118111158.0 | ||
| 090 | |a 676156 | ||
| 100 | |a 20241101d2023 k||y0rusy50 ca | ||
| 101 | 0 | |a eng |c rus | |
| 102 | |a KZ | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i |b e | |
| 182 | 0 | |a b | |
| 183 | 0 | |a cr |2 RDAcarrier | |
| 200 | 1 | |a Characterization of YAG:Ce ceramics with graphene oxide |d Характеристика керамики YAG:Ce с оксидом графена |f D. Deulina, V. Paygin, T. Alishin [et al.] |z rus | |
| 203 | |a Текст |c электронный |b визуальный | ||
| 283 | |a online_resource |2 RDAcarrier | ||
| 320 | |a References: 21 tit. | ||
| 330 | |a Yttrium-aluminum garnet (Y3Al5O12) is an optical material that shows great potential due to its favorable light-emitting and mechanical properties, as well as its chemical stability and thermal resistance. It is commonly utilized in laser technology, optical instruments, and solid-state light sources as a result of its activation by transition metal or rare earth element ions. In this work, experiments were carried out on the procedure for compacting samples of luminescent ceramics Y3Al5O12:Ce3+, by single-base pressing followed by sintering. Comprehensive studies of the influence of graphene oxide of variable concentration (x=0.1;0.5; 1 wt.%) on the radiative characteristics of ceramic samples. It was found that the addition of graphene oxide in an amount from 0.1 to 1 wt. % affects the density and luminescent properties of YAG:Ce ceramics. There is a decrease in the value of the density parameter at concentrations of graphene oxide 0.1-1 wt. % before annealing, after annealing, the relative density value increases to ~99 %. The luminescence spectrum when excited by a blue LED chip appears as a wide band in the spectral range 460-750, the nature of which is associated with radiative transitions in the cerium ion. It has been established that the light-emitting characteristics have a downward trend when activated by graphene oxide. The integral luminescence intensity decreases from 27.1 % to 19 % with an increase in the concentration of graphene oxide. | ||
| 330 | |a Иттрий-алюминиевый гранат (Y3Al5O12) является перспективным оптическим материалом с хорошими светоизлучающими и механическими свойствами, химической стабильностью и термической стойкостью. Материалы на основе иттрий-алюминиевого граната, активированного ионами переходных металлов или редкоземельных элементов, широко используются в лазерной технике, оптическом приборостроении и твердотельных источниках света. В настоящей работе были проведены эксперименты по процедуре компактирования образцов люминесцентной керамики Y3Al5O12:Ce3+, путем одноосновного прессования с последующим спеканием. Проведены комплексные исследования влияния оскида графена переменной концентрации (x=0,1; 0,5; 1 вес. %) на излучательные характеристики образцов керамики. Было установлено, что добавка оксида графена в количестве от 0,1 до 1 мас. % влияет на плотность и люминесцентные свойства YAG:Ce керамики. Наблюдается снижение значения параметра плотности при концентрациях оксида графена 0,1–1 вес. % до отжига, после отжига значение относительной плотности повышается до ~99%. Спектр люминесценции при возбуждении синий, чипом светодиода проявляется в виде широкой полосы в спектральном диапазоне 460–750, природа которой связана с излучательными переходами в ионе церия. Установлено, что светоизлучающие характеристики имеют динамику к снижению при активации оксидом графена. Интегральная интенсивность свечения уменьшается с 27,1до 19% при повышении концентрации оксида графена. | ||
| 336 | |a Текстовый файл | ||
| 461 | 1 | |t Вестник Карагандинского университета. Физика |f Карагандинский университет им. Е. А. Букетова |c Караганда |n КарГУ | |
| 463 | 1 | |t No 3 (111) |v С. 151-155 |d 2023 | |
| 610 | 1 | |a YAG ceramics | |
| 610 | 1 | |a sintering process | |
| 610 | 1 | |a graphene oxide | |
| 610 | 1 | |a mechanic properties | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 701 | 1 | |a Deulina |b D. E. |c specialist in the field of material science |c Research Engineer of Tomsk Polytechnic University |f 1999- |g Darjya Evgenjevna |9 88618 | |
| 701 | 1 | |a Paygin |b V. D. |c specialist in the field of material science |c engineer of Tomsk Polytechnic University |f 1992- |g Vladimir Denisovich |9 20806 | |
| 701 | 1 | |a Alishin |b T. R. |c specialist in the field of material science |c specialist on educational and methodical work of Tomsk Polytechnic University |f 1995- |g Timofey Ruslanovich |9 22038 | |
| 701 | 1 | |a Stepanov |b S. A. |c specialist in the field of lightning engineering |c Engineer of Tomsk Polytechnic University |f 1986- |g Sergey Aleksandrovich |9 17369 | |
| 701 | 1 | |a Valiev |b D. T. |c specialist in the field of material science |c Associate Professor of Tomsk Polytechnic University, Candidate of Physical and Mathematical Sciences |f 1987- |g Damir Talgatovich |9 17370 | |
| 701 | 1 | |a Dvilis |b E. S. |c Chemical Engineer |c senior researcher of Tomsk Polytechnic University, Professor, doctor of physical and mathematical Sciences |f 1969- |g Edgar Sergeevich |9 17959 | |
| 701 | 1 | |a Khasanov |b O. L. |c Russian physicist, materials scientist, Doctor of Engineering |c professor, Director of TPU Nano-Centre and Head of the Department "Nanomaterials and Nanotechnologies" of TPU |f 1958- |g Oleg Leonidovich |9 12652 | |
| 701 | 1 | |a Ilela |b A. E. |c specialist in the field of material science |c Assistant of the Department of Tomsk Polytechnic University |f 1982- |g Alfa Edison |9 21549 | |
| 801 | 2 | |a RU |b 63413507 |c 202401101 |g RCR | |
| 856 | 4 | |u https://doi.org/10.31489/2023ph3/151-155 |z https://doi.org/10.31489/2023ph3/151-155 | |
| 942 | |c CF | ||