Thermoelectric power properties of hydrogenated alloy Ti-6Al-4V subjected to mechanical impact and electron irradiation; Technical Physics; Vol. 69, No. 5
| Parent link: | Technical Physics.— .— Saint Petersburg: Ioffe Institute Vol. 69, No. 5.— 2024.— P. 705-709 |
|---|---|
| Autor principal: | |
| Autor corporatiu: | |
| Altres autors: | |
| Sumari: | Title screen The thermoelectric power properties of the Ti-6Al-4V alloy hydrogenated with hydrogen (hydrogen content 0.002 wt.% and 0.23 mass.%), subjected to mechanical rupture (up to 25 to 450 MPa) and irradiation with a pulsed electron flow with an energy of 18 keV to 25 J/cm2 and duration 15 μs. The role of individual Al and V components in relation to changes in the thermoelectric properties of the alloy is noted. Of interest is not only the stabilization of phases, but also the transformation of the alloy under study into a layered medium due to hydrogenation and fixation of hydrogen in traps. The change in the Seebeck coefficient S varies for different conditions in the range (from 0.0011 to 0.0030 mV/K. Due to its stability and strength properties, this kind of alloy can be suitable for use in systems for monitoring the properties of implants and non-traditional energy Исследованы термоэлектрические свойства гидрированного сплава Ti-6Al-4V (содержание водорода 0.002 и 0.23 mass.%), подвергнутому механическому разрыву (от 25 до 450 МРа) и облучению потоком электронов с энергией 18 keV, плотностью энергии до 25 J/cm2 и длительностью 15 μs. Отмечена роль отдельных компонент Al и V относительно изменения термоэлектрических свойств сплава. Представляют интерес не только стабилизация фаз, но и трансформация изучаемого сплава в слоистую среду, благодаря гидрированию и закреплению водорода в ловушках. Изменение коэффициента Зеебека S варьируется для различных условий в интервале от 0.0011 до 0.0030 mV/K и сопровождается инверсией знака термоэдс. Такого рода сплав может быть пригоден в силу стабильности и прочностных свойств для применения в системах контроля свойств имплантатов и нетрадиционной энергетики Текстовый файл |
| Idioma: | anglès |
| Publicat: |
2024
|
| Matèries: | |
| Accés en línia: | https://journals.ioffe.ru/articles/58520 Статья на русском языке |
| Format: | Electrònic Capítol de llibre |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=675756 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 675756 | ||
| 005 | 20241022092356.0 | ||
| 090 | |a 675756 | ||
| 100 | |a 20241022d2024 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i |b e | |
| 182 | 0 | |a b | |
| 183 | 0 | |a cr |2 RDAcarrier | |
| 200 | 1 | |a Thermoelectric power properties of hydrogenated alloy Ti-6Al-4V subjected to mechanical impact and electron irradiation |f V. V. Larionov, E. N. Stepanova |d Термоэлектрические свойства гидрированного сплава Ti-6Al-4V, подвергнутого механическому воздействию и облучению электронами |z rus | |
| 203 | |a Текст |c электронный |b визуальный | ||
| 283 | |a online_resource |2 RDAcarrier | ||
| 300 | |a Title screen | ||
| 320 | |a References: 24 tit. | ||
| 330 | |a The thermoelectric power properties of the Ti-6Al-4V alloy hydrogenated with hydrogen (hydrogen content 0.002 wt.% and 0.23 mass.%), subjected to mechanical rupture (up to 25 to 450 MPa) and irradiation with a pulsed electron flow with an energy of 18 keV to 25 J/cm2 and duration 15 μs. The role of individual Al and V components in relation to changes in the thermoelectric properties of the alloy is noted. Of interest is not only the stabilization of phases, but also the transformation of the alloy under study into a layered medium due to hydrogenation and fixation of hydrogen in traps. The change in the Seebeck coefficient S varies for different conditions in the range (from 0.0011 to 0.0030 mV/K. Due to its stability and strength properties, this kind of alloy can be suitable for use in systems for monitoring the properties of implants and non-traditional energy | ||
| 330 | |a Исследованы термоэлектрические свойства гидрированного сплава Ti-6Al-4V (содержание водорода 0.002 и 0.23 mass.%), подвергнутому механическому разрыву (от 25 до 450 МРа) и облучению потоком электронов с энергией 18 keV, плотностью энергии до 25 J/cm2 и длительностью 15 μs. Отмечена роль отдельных компонент Al и V относительно изменения термоэлектрических свойств сплава. Представляют интерес не только стабилизация фаз, но и трансформация изучаемого сплава в слоистую среду, благодаря гидрированию и закреплению водорода в ловушках. Изменение коэффициента Зеебека S варьируется для различных условий в интервале от 0.0011 до 0.0030 mV/K и сопровождается инверсией знака термоэдс. Такого рода сплав может быть пригоден в силу стабильности и прочностных свойств для применения в системах контроля свойств имплантатов и нетрадиционной энергетики | ||
| 336 | |a Текстовый файл | ||
| 461 | 1 | |t Technical Physics |c Saint Petersburg |n Ioffe Institute | |
| 463 | 1 | |t Vol. 69, No. 5 |v P. 705-709 |d 2024 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a thermoelectric power | |
| 610 | 1 | |a Seebeck coefficient | |
| 610 | 1 | |a pulsed electrons | |
| 610 | 1 | |a hydrogen | |
| 610 | 1 | |a термоэдс | |
| 610 | 1 | |a коэффициент Зеебека | |
| 610 | 1 | |a импульсные электроны | |
| 610 | 1 | |a водород | |
| 700 | 1 | |a Larionov |b V. V. |c physicist |c Professor of Tomsk Polytechnic University, Doctor of Pedagogical Sciences |f 1945- |g Vitaliy Vasilyevich |9 14653 | |
| 701 | 1 | |a Stepanova |b E. N. |c physicist |c Associate Professor of Tomsk Polytechnic University, Candidate of technical sciences |f 1981- |g Ekaterina Nikolaevna |9 18329 | |
| 712 | 0 | 2 | |a National Research Tomsk Polytechnic University |4 570 |9 27197 |
| 801 | 0 | |a RU |b 63413507 |c 20241022 |g RCR | |
| 856 | 4 | |u https://journals.ioffe.ru/articles/58520 |z https://journals.ioffe.ru/articles/58520 | |
| 856 | 4 | |u https://journals.ioffe.ru/articles/57814 |z Статья на русском языке | |
| 942 | |c CR | ||