Особенности аннигиляции позитронов в наноразмерных металлических слоях Zr/Nb после облучения протонами; Перспективы развития фундаментальных наук; Т. 1 : Физика
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XXI Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 23-26 апреля 2024 г./ Национальный исследовательский Томский политехнический университет ; под ред. И. А. Курзиной [и др.].— .— Томск: Изд-во ТПУ Т. 1 : Физика.— 2024.— С. 323-325 |
|---|---|
| Hlavní autor: | |
| Korporativní autor: | |
| Další autoři: | , |
| Shrnutí: | Заглавие с экрана Radiation damage limits the operating time of many structural materials under extreme conditions. Nanoscale multilayer coatings (NMCs) are a promising direction in developing materials that resist radiation damage and have improved physical and mechanical properties. This paper aims to experimentally understand changes in the defect structure of nanoscale multilayer coatings (NMCs) with alternating layers of Zr and Nb under irradiation. Zr/Nb NMCs with varying thicknesses of individual layers were fabricated using magnetron sputtering and then exposed to H+ irradiation. The evolution of the defect state under proton irradiation was studied using positron annihilation spectroscopy (PAS). The structural defects were analyzed using Doppler broadening spectroscopy (DBS) with a variable-energy positron beam. Irradiation causes destruction of interfaces when the thickness of individual layers is less than 25 nm. However, there is no significant increase in the defect level. The S parameter (amount of open volume defects) before and after irradiation remains practically unchanged. After irradiating NMC Zr/Nb with 50 and 100 nm thick layers, the microstructure remains unchanged and the S parameter is significantly reduced Текстовый файл |
| Jazyk: | ruština |
| Vydáno: |
2024
|
| Témata: | |
| On-line přístup: | http://earchive.tpu.ru/handle/11683/80604 |
| Médium: | Elektronický zdroj Kapitola |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=674725 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 674725 | ||
| 005 | 20251028071620.0 | ||
| 090 | |a 674725 | ||
| 100 | |a 20240919d2024 k||y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 200 | 1 | |a Особенности аннигиляции позитронов в наноразмерных металлических слоях Zr/Nb после облучения протонами |d Characteristics of the annihilation of positrons in nanoscale metal coatings Zr/Nb after proton irradiation |f Ц. Фань, А. Д. Ломыгин, Р. С. Лаптев |g науч. рук. Р. С. Лаптев ; Национальный исследовательский Томский политехнический университет |z eng | |
| 300 | |a Заглавие с экрана | ||
| 320 | |a Список литературы: 4 назв. | ||
| 330 | |a Radiation damage limits the operating time of many structural materials under extreme conditions. Nanoscale multilayer coatings (NMCs) are a promising direction in developing materials that resist radiation damage and have improved physical and mechanical properties. This paper aims to experimentally understand changes in the defect structure of nanoscale multilayer coatings (NMCs) with alternating layers of Zr and Nb under irradiation. Zr/Nb NMCs with varying thicknesses of individual layers were fabricated using magnetron sputtering and then exposed to H+ irradiation. The evolution of the defect state under proton irradiation was studied using positron annihilation spectroscopy (PAS). The structural defects were analyzed using Doppler broadening spectroscopy (DBS) with a variable-energy positron beam. Irradiation causes destruction of interfaces when the thickness of individual layers is less than 25 nm. However, there is no significant increase in the defect level. The S parameter (amount of open volume defects) before and after irradiation remains practically unchanged. After irradiating NMC Zr/Nb with 50 and 100 nm thick layers, the microstructure remains unchanged and the S parameter is significantly reduced | ||
| 336 | |a Текстовый файл | ||
| 461 | 1 | |0 674010 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XXI Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 23-26 апреля 2024 г. |9 674010 |c Томск |n Изд-во ТПУ |f Национальный исследовательский Томский политехнический университет ; под ред. И. А. Курзиной [и др.] | |
| 463 | 1 | |0 674235 |t Т. 1 : Физика |v С. 323-325 |d 2024 |9 674235 |p 1 файл (66,9 MB, 392 с.) |u conference_tpu-2024-C21_V1.pdf |l Vol. 1 : Physics | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a радиационные дефекты | |
| 610 | 1 | |a H+-облучение | |
| 610 | 1 | |a наноразмерные покрытия | |
| 610 | 1 | |a многослойные покрытия | |
| 610 | 1 | |a структурные материалы | |
| 700 | 1 | |a Фань |b Ц. | |
| 701 | 1 | |a Ломыгин |b А. Д. |c физик |c заведующий лабораторией Томского политехнического университета |f 1997- |g Антон Дмитриевич |9 21809 | |
| 701 | 1 | |a Лаптев |b Р. С. |c физик, специалист в области неразрушающего контроля |c доцент Томского политехнического университета, доктор технических наук |f 1987- |g Роман Сергеевич |y Томск |9 14396 | |
| 702 | 1 | |a Лаптев |b Р. С. |c физик, специалист в области неразрушающего контроля |c младший научный сотрудник Томского политехнического университета, ассистент, кандидат наук |f 1987- |g Роман Сергеевич | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |c (2009- ) |9 26305 |4 570 |
| 801 | 0 | |a RU |b 63413507 |c 202409019 |g RCR | |
| 856 | 4 | |z http://earchive.tpu.ru/handle/11683/80604 |u http://earchive.tpu.ru/handle/11683/80604 | |
| 942 | |c CF | ||