Исследование влияния содержания Si на деформацию и разрушение покрытий Ti-Al-Ta-Si-N при одноосном растяжении
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XXI Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 23-26 апреля 2024 г./ Национальный исследовательский Томский политехнический университет ; под ред. И. А. Курзиной [и др.].— .— Томск: Изд-во ТПУ Т. 1 : Физика.— 2024.— С. 206-208 |
|---|---|
| Päätekijä: | |
| Yhteisötekijä: | |
| Muut tekijät: | , , |
| Yhteenveto: | Заглавие с экрана The effect of Si alloying of Ti-Al-Ta-N coatings on their crack resistance and adhesive strength under uniaxial tension is investigated. It is shown that the hardness, reduced Young's modulus and residual compressive stresses increase with the addition of Si. The alloying is found to lead to a shift in the ultimate strain to failure towards larger values and an increase in the density of transverse cracks. It is also revealed that the shear strength of the interface between the Ti-Al-Ta-Si-N coatings and the steel substrate increases with increasing silicon content, reaching a maximum at 7.5 at. % Si Текстовый файл |
| Julkaistu: |
2024
|
| Aiheet: | |
| Linkit: | http://earchive.tpu.ru/handle/11683/80582 |
| Aineistotyyppi: | Elektroninen Kirjan osa |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=674428 |
| Yhteenveto: | Заглавие с экрана The effect of Si alloying of Ti-Al-Ta-N coatings on their crack resistance and adhesive strength under uniaxial tension is investigated. It is shown that the hardness, reduced Young's modulus and residual compressive stresses increase with the addition of Si. The alloying is found to lead to a shift in the ultimate strain to failure towards larger values and an increase in the density of transverse cracks. It is also revealed that the shear strength of the interface between the Ti-Al-Ta-Si-N coatings and the steel substrate increases with increasing silicon content, reaching a maximum at 7.5 at. % Si Текстовый файл |
|---|