Влияние режимов гибридной модификации сталей на их коррозионные свойства; Перспективы развития фундаментальных наук; Т. 1 : Физика
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XXI Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 23-26 апреля 2024 г./ Национальный исследовательский Томский политехнический университет ; под ред. И. А. Курзиной [и др.].— .— Томск: Изд-во ТПУ Т. 1 : Физика.— 2024.— С. 172-174 |
|---|---|
| Hovedforfatter: | |
| Institution som forfatter: | |
| Andre forfattere: | |
| Summary: | Заглавие с экрана In this study, the corrosion resistance of 20X13 and 38X2MYA steel samples subjected to hybrid modification, which included plasma nitriding performed at 480 °C for 180 minutes and thermal chemical and electrochemical oxidation, were evaluated. As a result of corrosion tests, calculations of the corrosion rate for all studied samples and polarization curve were obtained. It was found that the sample after chemical oxidation for 90 minutes (4,07*10-3 mm/year, 4,01*10-3 mm/year) has the lowest corrosion rate, and the sample of electrochemical oxidation has the highest (7,76*10-1 mm/year, 4,67*10-1 mm/year) Текстовый файл |
| Sprog: | russisk |
| Udgivet: |
2024
|
| Fag: | |
| Online adgang: | http://earchive.tpu.ru/handle/11683/80573 |
| Format: | Electronisk Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=674416 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 674416 | ||
| 005 | 20260715071743.0 | ||
| 090 | |a 674416 | ||
| 100 | |a 20240908d2024 k||y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 200 | 1 | |a Влияние режимов гибридной модификации сталей на их коррозионные свойства |d The effect of the modes of hybrid modification of steels on their corrosion properties |f Э. О. Квасович |g науч. рук. В. А. Грудинин ; Национальный исследовательский Томский политехнический университет |z eng | |
| 300 | |a Заглавие с экрана | ||
| 320 | |a Список литературы: 6 назв. | ||
| 330 | |a In this study, the corrosion resistance of 20X13 and 38X2MYA steel samples subjected to hybrid modification, which included plasma nitriding performed at 480 °C for 180 minutes and thermal chemical and electrochemical oxidation, were evaluated. As a result of corrosion tests, calculations of the corrosion rate for all studied samples and polarization curve were obtained. It was found that the sample after chemical oxidation for 90 minutes (4,07*10-3 mm/year, 4,01*10-3 mm/year) has the lowest corrosion rate, and the sample of electrochemical oxidation has the highest (7,76*10-1 mm/year, 4,67*10-1 mm/year) | ||
| 336 | |a Текстовый файл | ||
| 461 | 1 | |0 674010 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XXI Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 23-26 апреля 2024 г. |9 674010 |c Томск |n Изд-во ТПУ |f Национальный исследовательский Томский политехнический университет ; под ред. И. А. Курзиной [и др.] | |
| 463 | 1 | |0 674235 |t Т. 1 : Физика |v С. 172-174 |d 2024 |9 674235 |p 1 файл (66,9 MB, 392 с.) |u conference_tpu-2024-C21_V1.pdf |l Vol. 1 : Physics | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a коррозионная стойкость | |
| 610 | 1 | |a плазменное азотирование | |
| 610 | 1 | |a химическое окисление | |
| 610 | 1 | |a электрохимическое окисление | |
| 610 | 1 | |a коррозионные свойства | |
| 700 | 1 | |a Квасович |b Э. О. | |
| 702 | 1 | |a Грудинин |b В. А. |c физик |c инженер Томского политехнического университета |f 1995- |g Владислав Алексеевич |4 727 | |
| 712 | 0 | 2 | |a Томский политехнический университет |c 1991- |7 ca |8 rus |4 570 |9 26305 |
| 801 | 0 | |a RU |b 63413507 |c 20240908 |g RCR | |
| 856 | 4 | |z http://earchive.tpu.ru/handle/11683/80573 |u http://earchive.tpu.ru/handle/11683/80573 | |
| 942 | |c CF | ||