Особенности влияния изохронного отжига на дефектную структуру наноразмерных многослойных покрытий Zr/Nb после наводораживания; Перспективы развития фундаментальных наук; Т. 1 : Физика
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XXI Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 23-26 апреля 2024 г./ Национальный исследовательский Томский политехнический университет ; под ред. И. А. Курзиной [и др.].— .— Томск: Изд-во ТПУ Т. 1 : Физика.— 2024.— С. 88-90 |
|---|---|
| Hlavní autor: | |
| Korporativní autor: | |
| Další autoři: | , |
| Shrnutí: | Заглавие с экрана The development of radiation-resistant materials is an important challenge to improve safety and extend the lifetime of structures. Researchers propose the use of nanoscale multilayer coatings (NMCs) that are resistant to radiation damage and have the ability to repair defects across interfaces. Multilayer barriers such as Cu/V, Al/Nb, Cu/Mo and Fe/W effectively retain defect clusters and reduce radiation damage. HCP/BCC Zr/Nb interfaces can prevent defect formation when exposed to proton radiation. However, hydrogen embrittlement of Zr alloys is a problem. To increase the lifetime of nuclear reactors, the problem of reducing hydrogen embrittlement of zirconium components of reactor cores must be addressed. However, most of the works on irradiation of multilayer structures have only considered the structure after interaction with helium ions and proton beams. The aim of this work is to investigate the effect of isochronous annealing on the defect structure of nanoscale Zr/Nb multilayer coatings after hydrogenation Текстовый файл |
| Jazyk: | ruština |
| Vydáno: |
2024
|
| Témata: | |
| On-line přístup: | http://earchive.tpu.ru/handle/11683/80551 |
| Médium: | Elektronický zdroj Kapitola |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=674370 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 674370 | ||
| 005 | 20251028071620.0 | ||
| 090 | |a 674370 | ||
| 100 | |a 20240905d2024 k||y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 200 | 1 | |a Особенности влияния изохронного отжига на дефектную структуру наноразмерных многослойных покрытий Zr/Nb после наводораживания |d Characteristics of the influence of isochronous annealing on the defect structure of nanoscale multilayer coatings Zr/Nb after hydrogenation |f Ч. Ван, А. Д. Ломыгин, Р. С. Лаптев |g науч. рук. Р. С. Лаптев ; Национальный исследовательский Томский политехнический университет |z eng | |
| 300 | |a Заглавие с экрана | ||
| 320 | |a Список литературы: 6 назв. | ||
| 330 | |a The development of radiation-resistant materials is an important challenge to improve safety and extend the lifetime of structures. Researchers propose the use of nanoscale multilayer coatings (NMCs) that are resistant to radiation damage and have the ability to repair defects across interfaces. Multilayer barriers such as Cu/V, Al/Nb, Cu/Mo and Fe/W effectively retain defect clusters and reduce radiation damage. HCP/BCC Zr/Nb interfaces can prevent defect formation when exposed to proton radiation. However, hydrogen embrittlement of Zr alloys is a problem. To increase the lifetime of nuclear reactors, the problem of reducing hydrogen embrittlement of zirconium components of reactor cores must be addressed. However, most of the works on irradiation of multilayer structures have only considered the structure after interaction with helium ions and proton beams. The aim of this work is to investigate the effect of isochronous annealing on the defect structure of nanoscale Zr/Nb multilayer coatings after hydrogenation | ||
| 336 | |a Текстовый файл | ||
| 461 | 1 | |0 674010 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XXI Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 23-26 апреля 2024 г. |9 674010 |c Томск |n Изд-во ТПУ |f Национальный исследовательский Томский политехнический университет ; под ред. И. А. Курзиной [и др.] | |
| 463 | 1 | |0 674235 |t Т. 1 : Физика |v С. 88-90 |d 2024 |9 674235 |p 1 файл (66,9 MB, 392 с.) |u conference_tpu-2024-C21_V1.pdf |l Vol. 1 : Physics | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a изохронный отжиг | |
| 610 | 1 | |a гидрирование | |
| 610 | 1 | |a аннигиляция позитронов | |
| 610 | 1 | |a многослойные покрытия | |
| 610 | 1 | |a наноразмерные покрытия | |
| 700 | 1 | |a Ван |b Ч. | |
| 701 | 1 | |a Ломыгин |b А. Д. |c физик |c заведующий лабораторией Томского политехнического университета |f 1997- |g Антон Дмитриевич |9 21809 | |
| 701 | 1 | |a Лаптев |b Р. С. |c физик, специалист в области неразрушающего контроля |c доцент Томского политехнического университета, доктор технических наук |f 1987- |g Роман Сергеевич |y Томск |9 14396 | |
| 702 | 1 | |a Лаптев |b Р. С. |c физик, специалист в области неразрушающего контроля |c младший научный сотрудник Томского политехнического университета, ассистент, кандидат наук |f 1987- |g Роман Сергеевич |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |c (2009- ) |9 26305 |4 570 |
| 801 | 0 | |a RU |b 63413507 |c 20240905 |g RCR | |
| 856 | 4 | |z http://earchive.tpu.ru/handle/11683/80551 |u http://earchive.tpu.ru/handle/11683/80551 | |
| 942 | |c CF | ||