Формирование пористой матрицы для остеозамещения на основе ZrO2
| Parent link: | Курзина, И. А. (химик ; 1972-). Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XXI Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 23-26 апреля 2024 г..— .— Томск: Изд-во ТПУ Т. 2 : Химия.— 2024.— С. 301-303 |
|---|---|
| Main Author: | |
| Corporate Author: | |
| Other Authors: | , |
| Summary: | Заглавие с экрана During the study porous ceramic scaffolds were obtained. The volumetric shrinkage after sintering amounted to about 50 %. The analysis of microstructural characteristics of the samples revealed a bimodal distribution of pores: macropores duplicate the morphology of pore-forming particles, and micropores are formed due to the fusion of interparticle voids and channels during the pressing process. The pore space is not through and has an isolated structure. According to the data of mechanical tests, the strength and modulus of elasticity of the investigated samples are in the range of values of strength and modulus of elasticity of bone tissue Текстовый файл |
| Language: | Russian |
| Published: |
2024
|
| Subjects: | |
| Online Access: | http://earchive.tpu.ru/handle/11683/80528 |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=674086 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 674086 | ||
| 005 | 20241120102121.0 | ||
| 090 | |a 674086 | ||
| 100 | |a 20240814d2024 k||y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 200 | 1 | |a Формирование пористой матрицы для остеозамещения на основе ZrO2 |d Formation of porous matrix for osteo-replacement based on ZrO2 |f Чжао Цзяхао, А. С. Буяков, Е. И. Сенькина |g науч. рук. А. С. Буяков ; Национальный исследовательский Томский политехнический университет |z eng | |
| 300 | |a Заглавие с экрана | ||
| 320 | |a Список литературы: 3 назв. | ||
| 330 | |a During the study porous ceramic scaffolds were obtained. The volumetric shrinkage after sintering amounted to about 50 %. The analysis of microstructural characteristics of the samples revealed a bimodal distribution of pores: macropores duplicate the morphology of pore-forming particles, and micropores are formed due to the fusion of interparticle voids and channels during the pressing process. The pore space is not through and has an isolated structure. According to the data of mechanical tests, the strength and modulus of elasticity of the investigated samples are in the range of values of strength and modulus of elasticity of bone tissue | ||
| 336 | |a Текстовый файл | ||
| 461 | 1 | |0 674010 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XXI Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 23-26 апреля 2024 г. |9 674010 |a Курзина, И. А. (химик ; 1972-) |c Томск |n Изд-во ТПУ | |
| 463 | 1 | |0 674011 |t Т. 2 : Химия |v С. 301-303 |d 2024 |9 674011 |p 1 файл (59,5 MB, 313 с.) |u conference_tpu-2024-C21_V2.pdf |l Volume 2 : Chemistry | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a zirconium dioxide | |
| 610 | 1 | |a strength | |
| 610 | 1 | |a porous ceramics | |
| 610 | 1 | |a osteo-replacement | |
| 700 | 0 | |a Чжао Цзяхао | |
| 701 | 1 | |a Буяков |b А. С. |g Алесь Сергеевич |c специалист в области материаловедения |c ассистент кафедры Томского политехнического университета |f 1992- |y Томск |9 21065 | |
| 701 | 1 | |a Сенькина |b Е. И. | |
| 702 | 1 | |a Буяков |b А. С. |c специалист в области материаловедения |c ассистент кафедры Томского политехнического университета |f 1992- |g Алесь Сергеевич |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |c (2009- ) |9 26305 |4 570 |
| 801 | 0 | |a RU |b 63413507 |c 20240814 |g RCR | |
| 856 | 4 | |z http://earchive.tpu.ru/handle/11683/80528 |u http://earchive.tpu.ru/handle/11683/80528 | |
| 942 | |c CF | ||