Консолидирование и физико-механические свойства керамики на основе карбонитрида циркония; Перспективы развития фундаментальных наук; Т. 2 : Химия
| Parent link: | Курзина, И. А. (химик ; 1972-). Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XXI Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 23-26 апреля 2024 г..— .— Томск: Изд-во ТПУ Т. 2 : Химия.— 2024.— С. 152-154 |
|---|---|
| প্রধান লেখক: | |
| সংস্থা লেখক: | |
| অন্যান্য লেখক: | |
| সংক্ষিপ্ত: | Заглавие с экрана The paper studied the physical and mechanical properties of ceramics based on zirconium carbonitride, consolidated by hot pressing. Consolidation was carried out at a temperature of 2000 ℃. It has been established that the complication of the crystal chemical structure leads to an increase in mechanical properties, but also leads to an increase in the porosity of the samples. During the research, such mechanical properties as the Vickers hardness of the samples and the elastic modulus of the samples were determined. It was found that among the studied samples, ceramics with an equimolar composition of zirconium carbide and zirconium nitride have the highest hardness. Moreover, this sample had the highest porosity and the highest elastic modulus Текстовый файл |
| ভাষা: | রুশ |
| প্রকাশিত: |
2024
|
| বিষয়গুলি: | |
| অনলাইন ব্যবহার করুন: | http://earchive.tpu.ru/handle/11683/80517 |
| বিন্যাস: | বৈদ্যুতিক গ্রন্থের অধ্যায় |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=674032 |
| সংক্ষিপ্ত: | Заглавие с экрана The paper studied the physical and mechanical properties of ceramics based on zirconium carbonitride, consolidated by hot pressing. Consolidation was carried out at a temperature of 2000 ℃. It has been established that the complication of the crystal chemical structure leads to an increase in mechanical properties, but also leads to an increase in the porosity of the samples. During the research, such mechanical properties as the Vickers hardness of the samples and the elastic modulus of the samples were determined. It was found that among the studied samples, ceramics with an equimolar composition of zirconium carbide and zirconium nitride have the highest hardness. Moreover, this sample had the highest porosity and the highest elastic modulus Текстовый файл |
|---|