Change in thermochemical properties of aluminum nanopowders upon irradiation with electron beam and microwave
| Parent link: | Курзина, И. А. (химик ; 1972-). Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XXI Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 23-26 апреля 2024 г..— .— Томск: Изд-во ТПУ Т. 2 : Химия.— 2024.— С. 14-16 |
|---|---|
| Tác giả chính: | |
| Tác giả của công ty: | |
| Tác giả khác: | |
| Tóm tắt: | Title screen In this work, aluminum nanopowder samples were irradiated with electron beam and microwave radiation of varying dose to ascertain their effect on thermophysical properties of metal powders. The results from the differential thermal analysis of the irradiated samples shows the highest value of thermal heat of oxidation (13678J/g) in the sample irradiated with microwave of (100J/50Hz ) with a corresponding highest peak temperature of oxidation (625⁰C). Based on the obtained experimental results, no correlation was observed between oxidation onset temperature and thermal effect of oxidation Текстовый файл |
| Được phát hành: |
2024
|
| Những chủ đề: | |
| Truy cập trực tuyến: | http://earchive.tpu.ru/handle/11683/80546 |
| Định dạng: | Điện tử Chương của sách |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=674016 |
| Tóm tắt: | Title screen In this work, aluminum nanopowder samples were irradiated with electron beam and microwave radiation of varying dose to ascertain their effect on thermophysical properties of metal powders. The results from the differential thermal analysis of the irradiated samples shows the highest value of thermal heat of oxidation (13678J/g) in the sample irradiated with microwave of (100J/50Hz ) with a corresponding highest peak temperature of oxidation (625⁰C). Based on the obtained experimental results, no correlation was observed between oxidation onset temperature and thermal effect of oxidation Текстовый файл |
|---|