Термическая обработка изделий титанового сплава ВТ14, полученных прокаткой и методом электронно-лучевой проволочной аддитивной
| Parent link: | Курзина, И. А. (химик ; 1972-). Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XX Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 25-28 апреля 2023 г..— .— Томск: Изд-во ТПУ, 2023 Т. 1 : Физика.— 2023.— С. 252-254 |
|---|---|
| Main Author: | |
| Corporate Author: | |
| Other Authors: | |
| Summary: | Заглавие с экрана The influence of the initial state of samples of titanium alloy VT14 produced by rolling and electron-beam additive technology on the change in their microstructure and mechanical properties during heat treatment was studied using optical microscopy and X-ray diffraction analysis. The results showed that during heat treatment the prior β grains size did not change, but the interlayers of residual β phase in the rolled products decreased, and in the 3D-printed samples the size of the α plates changed. During heat treatment, the β-phase content decreased in all samples and the ω-phase completely disappeared Текстовый файл |
| Language: | Russian |
| Published: |
2023
|
| Subjects: | |
| Online Access: | http://earchive.tpu.ru/handle/11683/80811 |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=673296 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 673296 | ||
| 005 | 20241101132921.0 | ||
| 090 | |a 673296 | ||
| 100 | |a 20240624d2023 k||y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 200 | 1 | |a Термическая обработка изделий титанового сплава ВТ14, полученных прокаткой и методом электронно-лучевой проволочной аддитивной |f Т. А. Лобова |g науч. рук. А. В. Панин ; Инженерная школа новых производственных технологий НИ ТПУ |d Heat treatment of hot-rolled and electron beam additive manufacturrd VT14 titanium alloy |z eng | |
| 300 | |a Заглавие с экрана | ||
| 320 | |a Библиография: с. 254 | ||
| 330 | |a The influence of the initial state of samples of titanium alloy VT14 produced by rolling and electron-beam additive technology on the change in their microstructure and mechanical properties during heat treatment was studied using optical microscopy and X-ray diffraction analysis. The results showed that during heat treatment the prior β grains size did not change, but the interlayers of residual β phase in the rolled products decreased, and in the 3D-printed samples the size of the α plates changed. During heat treatment, the β-phase content decreased in all samples and the ω-phase completely disappeared | ||
| 336 | |a Текстовый файл | ||
| 461 | 1 | |0 636133 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XX Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 25-28 апреля 2023 г. |d 2023 |9 636133 |a Курзина, И. А. (химик ; 1972-) |c Томск |n Изд-во ТПУ | |
| 463 | 1 | |0 669915 |t Т. 1 : Физика |v С. 252-254 |d 2023 |9 669915 |p 1 файл (75,9 MB, 442 с.) |u conference_tpu-2023-C21_V1.pdf |l Volume 1. Physics | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a титановые сплавы | |
| 610 | 1 | |a ВТ14 | |
| 610 | 1 | |a термическая обработка | |
| 610 | 1 | |a рентгеноструктурный анализ | |
| 610 | 1 | |a микротвердость | |
| 610 | 1 | |a микроструктура | |
| 610 | 1 | |a прокатанные образцы | |
| 700 | 1 | |a Лобова |b Т. А. | |
| 702 | 1 | |a Панин |b А. В. |c физик |c профессор Томского политехнического университета, доктор физико-математических наук |f 1971- |g Алексей Викторович |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа ядерных технологий |b Отделение экспериментальной физики |9 28346 |
| 801 | 0 | |a RU |b 63413507 |c 20240624 |g RCR | |
| 856 | 4 | |z http://earchive.tpu.ru/handle/11683/80811 |u http://earchive.tpu.ru/handle/11683/80811 | |
| 942 | |c CF | ||