Термическая обработка изделий титанового сплава ВТ14, полученных прокаткой и методом электронно-лучевой проволочной аддитивной
| Parent link: | Курзина, И. А. (химик ; 1972-). Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XX Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 25-28 апреля 2023 г..— .— Томск: Изд-во ТПУ, 2023 Т. 1 : Физика.— 2023.— С. 252-254 |
|---|---|
| المؤلف الرئيسي: | |
| مؤلف مشترك: | |
| مؤلفون آخرون: | |
| الملخص: | Заглавие с экрана The influence of the initial state of samples of titanium alloy VT14 produced by rolling and electron-beam additive technology on the change in their microstructure and mechanical properties during heat treatment was studied using optical microscopy and X-ray diffraction analysis. The results showed that during heat treatment the prior β grains size did not change, but the interlayers of residual β phase in the rolled products decreased, and in the 3D-printed samples the size of the α plates changed. During heat treatment, the β-phase content decreased in all samples and the ω-phase completely disappeared Текстовый файл |
| منشور في: |
2023
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | http://earchive.tpu.ru/handle/11683/80811 |
| التنسيق: | الكتروني فصل الكتاب |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=673296 |
| الملخص: | Заглавие с экрана The influence of the initial state of samples of titanium alloy VT14 produced by rolling and electron-beam additive technology on the change in their microstructure and mechanical properties during heat treatment was studied using optical microscopy and X-ray diffraction analysis. The results showed that during heat treatment the prior β grains size did not change, but the interlayers of residual β phase in the rolled products decreased, and in the 3D-printed samples the size of the α plates changed. During heat treatment, the β-phase content decreased in all samples and the ω-phase completely disappeared Текстовый файл |
|---|