High-Temperature Oxidation of a Zr–1Nb Alloy with a Protective Cr/Ta Coating

High-Temperature Oxidation of a Zr–1Nb Alloy with a Protective Cr/Ta Coating

Detaylı Bibliyografya
Parent link:	Journal of Surface Investigation. X-ray, Synchrotron and Neutron Techniques.— .— New York: Springer Science Vol. 17, Supplement 1.— 2023.— P. 115-120
Müşterek Yazar:	National Research Tomsk Polytechnic University
Diğer Yazarlar:	Syrtanov M. S. Maksim Sergeevich, Korneev S. P. Stepan Pavlovich, Abdulmenova A. V. Anastasiya Vladimirovna, Lomygin A. D. Anton Dmitrievich, Mishchenko D. D. Denis Dmitrievich
Özet:	The oxidation and interdiffusion mechanisms of a Zr–1Nb zirconium alloy with a Cr/Ta coating have been investigated. Multilayer Cr(8 μm)/Ta(3 μm) coatings were deposited by magnetron sputtering. The coated zirconium alloy samples were oxidized at 1100°C without isothermal exposure and under exposure for 15–60 min. The coating ceased to act as a diffusion barrier and, consequently, began to delaminate at 60 min of oxidation. Studies on the protective properties of the Cr/Ta coatings were carried out using XRD, SEM, and in situ XRD up to 1250°C. The results showed that during the oxidation process, tantalum diffused into both chromium with the formation of the Cr2Ta phase and zirconium. In situ XRD indicated the formation of the Cr2Zr phase during oxidation for 2 min at 1250°C. The thickness of the residual chromium layer in the case of the Cr/Ta coating was greater than that of the single-layer chromium coating. The possibilities of using Cr/Ta as a coating for fuel cladding were considered. Текстовый файл
Baskı/Yayın Bilgisi:	2023
Konular:	magnetron sputtering multilayer coatings zirconium alloy chromium tantalum diffusion barrier high–temperature oxidation in situ X-ray diffraction interdiffusion corrosion resistance труды учёных ТПУ электронный ресурс
Online Erişim:	https://doi.org/10.1134/S1027451023070510
Materyal Türü:	Elektronik Kitap Bölümü
KOHA link:	https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=672693

Benzer Materyaller

Barrier Properties of Cr/Ta-Coated Zr-1Nb Alloy under High-Temperature Oxidation
Baskı/Yayın Bilgisi: (2024)

High-temperature oxidation of Zrsingle bond1Nb zirconium alloy with protective Cr/Mo coating
Baskı/Yayın Bilgisi: (2022)

ZrO2/Cr Multilayer Coating for the Protection of E110 Zirconium Alloy from High Temperatures
Baskı/Yayın Bilgisi: (2023)

Effect of Molybdenum Texture on the High-Temperature Oxidation Resistance of Zr–1Nb Alloy with a Cr/Mo Coating
Baskı/Yayın Bilgisi: (2023)

Non-destructive testing of a Zr–1Nb zirconium alloy with a protective Cr/Mo thin layers coating for the production components of corrosion-resistant for nuclear reactors
Yazar:: Salman A. M.
Baskı/Yayın Bilgisi: (2024)

Protective Cr coatings with CrN/Cr multilayers for zirconium fuel claddings
Baskı/Yayın Bilgisi: (2022)

Protection of Zr Alloy under High-Temperature Air Oxidation: A Multilayer Coating Approach
Baskı/Yayın Bilgisi: (2021)

Low resistivity measurement of chromium coatings on zirconium alloys E110 for the production of accident-resistant core components of nuclear reactors
Yazar:: Salman A. M. Abdelrakhman Mokhamed Abbas Ali
Baskı/Yayın Bilgisi: (2025)

Protective Cr Coatings with ZrO2/Cr Multilayers for Zirconium Fuel Claddings
Baskı/Yayın Bilgisi: (2022)

Microstructure characterization and corrosion behaviour of a nanohydroxyapatite coating deposited on AZ31 magnesium
Yazar:: Surmeneva M. A. Maria Alexandrovna
Baskı/Yayın Bilgisi: (2015)

On the Gas-Phase Hydrogenation of E110 Zirconium Alloy with a Chromium Coating
Baskı/Yayın Bilgisi: (2024)

Non-destructive techniques on zirconium alloy E110 with chromium coatings for the production of emergency-resistant core components of nuclear reactors
Yazar:: Salman A. M.
Baskı/Yayın Bilgisi: (2024)

Recent Advances in Protective Coatings for Accident Tolerant Zr-Based Fuel Claddings
Baskı/Yayın Bilgisi: (2021)

Oxidation kinetics of Cr-coated zirconium alloy: Effect of coating thickness and microstructure
Baskı/Yayın Bilgisi: (2020)

High-Temperature Steam Oxidation of Accident-Tolerant Cr/Mo-Coated Zr Alloy at 1200–1400 °C
Baskı/Yayın Bilgisi: (2023)

A comparative study on high-temperature air oxidation of Cr-coated E110 zirconium alloy deposited by magnetron sputtering and electroplating
Baskı/Yayın Bilgisi: (2022)

Effect of Irradiation with a Pulsed Electron Beam on Chromium Diffusion in the Zr–1 wt % Nb Alloy
Baskı/Yayın Bilgisi: (2024)

Influence of coating parameters on oxidation behavior of Cr-coated zirconium alloy for accident tolerant fuel claddings
Baskı/Yayın Bilgisi: (2022)

Hydrogenation Behavior of Cr-Coated Resistance Upset Welds of E110 Zirconium Alloy
Baskı/Yayın Bilgisi: (2023)

Oxidation and Mechanical Behavior of Cr-Coated Laser Beam Welds Made from E110 Zirconium Alloy
Baskı/Yayın Bilgisi: (2022)

High-Temperature Oxidation of Cr-Coated Resistance Upset Welds Made from E110 Alloy
Yazar:: Sidelev D. V. Dmitry Vladimirovich
Baskı/Yayın Bilgisi: (2021)

Chromium coatings deposited by cooled and hot target magnetron sputtering for accident tolerant nuclear fuel claddings
Baskı/Yayın Bilgisi: (2020)

Effect of Hydrogen on Grain Boundary Diffusion of Chromium in Zr–1 wt % Nb Alloy
Baskı/Yayın Bilgisi: (2025)

Deposition temperature effect on sputtered hydroxyapatite coatings prepared on AZ31B alloy substrate
Baskı/Yayın Bilgisi: (2022)

Magnetron Deposition of Cr Coatings with RF-ICP Assistance
Baskı/Yayın Bilgisi: (2022)

Hydrogenation behavior of Cr-coated laser beam welds of E110 zirconium alloy
Baskı/Yayın Bilgisi: (2022)

Fabrication of customizable wedged multilayer Laue lenses by adding a stress layer
Baskı/Yayın Bilgisi: (2015)

Improvement of CoCr Alloy Characteristics by Ti-Based Carbonitride Coatings Used in Orthopedic Applications
Baskı/Yayın Bilgisi: (2020)

Hydrogen Sorption Kinetics of SiC-Coated Zr-1Nb Alloy
Baskı/Yayın Bilgisi: (2019)

In Situ Study of Hydrogen Accumulation in the E110 Zirconium Alloy during Gas-Phase Hydrogenation by the Methods of Thermal Desorption Spectroscopy and Synchrotron X-Ray Diffraction Analysis
Baskı/Yayın Bilgisi: (2023)

Influence of Nitrogen on Corrosion Resistance of Thin Ti–O–N Films Deposited by Reactive Magnetron Sputtering
Yazar:: Boytsova E. L. Elena Lvovna
Baskı/Yayın Bilgisi: (2021)

Nickel-chromium (Ni–Cr) coatings deposited by magnetron sputtering for accident tolerant nuclear fuel claddings
Baskı/Yayın Bilgisi: (2019)

The release of nickel from nickel-titanium (NiTi) is strongly reduced by a sub-micrometer thin layer of calcium phosphate deposited by rf-magnetron sputtering
Baskı/Yayın Bilgisi: (2010)

Effect of Annealing on the Microstructure and Structural-Phase State of Nanoscale Multilayer Zr/Nb Coatings after Irradiation with He+ Ions
Baskı/Yayın Bilgisi: (2024)

Effects of annealing in vacuum on the microstructure of silicon-containing calcium phosphate films deposited on a ZrNb alloy by radio-frequency magnetron sputtering
Baskı/Yayın Bilgisi: (2023)

Multiscale design of an additively manufactured Ti–Nb alloy with nanostructured Sr-substituted hydroxyapatite coating for bone tissue engineering
Baskı/Yayın Bilgisi: (2025)

A Review of Magnesium Alloys In Vivo Antibacterial Properties: Challenges, Solutions, and Perspectives in Implant-Associated Orthopedic Infections
Baskı/Yayın Bilgisi: (2025)

Structure, mechanical and tribological properties of Ti-doped and Cr-doped a-C:H:SiOx coatings
Baskı/Yayın Bilgisi: (2024)

Thermal stability and oxidation resistance of ZrSiN nanocomposite and ZrN/SiNx multilayered coatings: A comparative study
Baskı/Yayın Bilgisi: (2017)

Magnetron deposition of chromium nitride coatings using a hot chromium target: Influence of magnetron power on the deposition rate and elemental composition
Baskı/Yayın Bilgisi: (2022)