Разработка мембран на основе MAX-фаз для очистки водорода
| Parent link: | Курзина, И. А. (химик ; 1972-). Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XX Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 25-28 апреля 2023 г..— .— Томск: Изд-во ТПУ, 2023 Т. 1 : Физика.— 2023.— С. 165-167 |
|---|---|
| Main Author: | |
| Corporate Author: | |
| Other Authors: | , , |
| Summary: | Заглавие с экрана The Ti3Al(Si)C2-based membranes from filled preceramic papers were fabricated by spark plasma sintering at different parameters. XRD analysis showed that all sintered samples consist of Ti3Al(Si)C2,, TiC, and Al2O3 phases. SEM was used to analyze microstructure of the samples. In addition, hydrogen permeability tests were carried out at 25 and 350 °C. The best performance was achieved by a membrane sintered at 1000°C and 5Pa. The hydrogen permeability and flux at 25 °C were 9,65∙10-9 molH2/(m∙s∙Pa) and 1,2 mol/(m2∙s) respectively Текстовый файл |
| Language: | Russian |
| Published: |
2023
|
| Subjects: | |
| Online Access: | http://earchive.tpu.ru/handle/11683/80797 |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=672553 |
| Summary: | Заглавие с экрана The Ti3Al(Si)C2-based membranes from filled preceramic papers were fabricated by spark plasma sintering at different parameters. XRD analysis showed that all sintered samples consist of Ti3Al(Si)C2,, TiC, and Al2O3 phases. SEM was used to analyze microstructure of the samples. In addition, hydrogen permeability tests were carried out at 25 and 350 °C. The best performance was achieved by a membrane sintered at 1000°C and 5Pa. The hydrogen permeability and flux at 25 °C were 9,65∙10-9 molH2/(m∙s∙Pa) and 1,2 mol/(m2∙s) respectively Текстовый файл |
|---|